Abstract:The extremely large magnetoresistance (XMR) observed in many topologically nontrivial and trivial semimetals has attracted much attention in relation to its underlying physical mechanism. In this paper, by combining the band structure and Fermi surface (FS) calculations with the Hall resistivity and de Haas-van Alphen (dHvA) oscillation measurements, we studied the anisotropy of magnetoresistance (MR) of ReO3 with a simple cubic structure, an "ordinary" nonmagnetic metal considered previously. We found that ReO3 exhibits almost all the characteristics of XMR semimetals: the nearly quadratic field dependence of MR, a field-induced upturn in resistivity followed by a plateau at low temperatures, and high mobilities of charge carriers. It was found that for magnetic field H applied along the c axis, the MR exhibits an unsaturated H-1.75 dependence, which was argued to arise from the complete carrier compensation supported by the Hall resistivity measurements. For H applied along the direction of 15 degrees relative to the c axis, an unsaturated H-1.90 dependence of MR up to (9.43 x 10(3))% at 10 K and 9 T was observed, which was explained by the existence of electron open orbits extending along the k(x) direction. Two mechanisms responsible for XMR observed usually in the semimetals occur also in the simple metal ReO3 due to its peculiar FS (two closed electron pockets and one open electron pocket), once again indicating that the details of FS geometrical configuration are a key factor for the observed XMR in materials.

Large Magnetoresistance in Ni1–xVxS

Large Magnetoresistance and Field-Induced Transition in Ni1-xRhxS

Large Magnetoresistance in Ni1−xFexS Near Room Temperature

Large Field-Induced Magnetocaloric Effect in Ni$_{43}$Mn$_{46 - {\rm X}}$v$_{\rm X}$sn$_{11}$ Heusler Alloys

In-plane Anisotropic Magnetoresistance in Detwinned BaFe_2-xNi_xAs_2 (x = 0, 0.6)

Large Field-Induced Magnetocaloric Effect in Ni<formula formulatype="inline"><tex Notation="TeX">$_{43}$</tex> </formula>Mn<formula formulatype="inline"><tex Notation="TeX">$_{46 - {\rm x}}$</tex></formula>V<formula formulatype="inline"><tex Notation="TeX">$_{\rm x}$</tex></formula>Sn<formula formul

In-plane Anisotropic Magnetoresistance in Detwinned BaFe2-xNixAs2 (x=0, 0.6)

Large Room-Temperature Magnetoresistance In Ultra-Thin La0.67sr0.33mno3/Nb : Srtio3 Junction

Large room-temperature magnetoresistance in ultra-thin La<sub>0.67</sub>Sr<sub>0.33</sub>MnO<sub>3</sub>/Nb : SrTiO<sub>3</sub>junction

Large Magnetoresistance and Large Magnetothermopower Effect in the Dirac Material EuMn0.8Sb2.

Extremely large magnetoresistance in the "ordinary" metal ReO<sub>3</sub>

Giant Magnetoresistance in Nis

Field-induced Metamagnetic Transition and Nonsaturating Magnetoresistance in the Antiferromagnetic Semimetal NdSb

Magnetism And Magnetoresistance Studies Of Hffe6ge6-Type Y1-Xcexmn6sn6 (X=0.1-0.3) Compounds

Magnetic and Transport Property Studies of Nanocrystalline ZnxFe3−xO4

Magnetoresistance and Kondo Effect in Nodal-Line Semimetal VAs2 *

Composition dependence of magnetoresistance in Fe$_{1-x}$Ni$_{x}$ alloys

Large Magnetoresistance over an Entire Region from 5 to 380 K in Double Helical Comnsi Compound

Intrinsic V Vacancy and Large Magnetoresistance in V 1-Δ Sb 2 Single Crystal

Topological Phase Transition-Induced Tri-Axial Vector Magnetoresistance in (Bi1-Xinx)2se3 Nanodevices

Very large magnetoresistance in Fe 0.28 TaS 2 single crystals