Microstructure and mechanical properties of the CaO-Al2O3-SiO2 system glass-ceramics
Xiangzhong Ren,Xianwen Yi,Yong Zhang,Yan Liu,Peixin Zhang,Jianhong Liu
DOI: https://doi.org/10.3724/SP.J.1249.2013.03319
2013-01-01
Shenzhen Daxue Xuebao (Ligong Ban)/Journal of Shenzhen University Science and Engineering
Abstract:CaO-Al2O3-SiO2 system (CAS) glass-ceramics with anorthite crystal structure was prepared by melt-method. Its microstructure and morphology were characterized by differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscope (SEM). The effects of TiO2 content on the relationship between microstructure and mechanical properties for the CAS glass-ceramics were also investigated by electron paramagnetic resonance (EPR) and the position annihilation technique (PAT). The results showed that the TiO2 content does not affect the type of the main crystalline phase of CAS glass-ceramics, but it could reduce the crystallization peak temperature and promote the crystallization. The relationship between g factor and bending strength showed that during the melting and heat-treatment process, part of the Ti4+ ions were reduced to Ti3+ and formed oxygen vacancies, the spin angular correlation between Ti3+-O-Ti3+ and oxygen vacancies affected the bending strength directly. The relationship between positron lifetime and bending strength showed that interval Ti4+ could make some defects and Al, Si vacancies, which could affect the mechanical properties. Electrostatic interaction between Ti4+ and O2- could make the independent oxonium ion into an integral, which was favourable to bending strength. When the TiO2 content was higher than 6%, some Si4+ were substituted by Ti4+, and the Ti-O bond was weaker than the Si-O bond, which led to a decrease in bending strength. When the content was 6%, the microhardness was 830 MPa, and the bending strength was 314 MPa in the heat treatment conditions of nucleation temperature 750°C, nucleation time 2 h, crystallization temperature 950°C, crystallization time 2 h.