Effects of different plasticizers on properties of gellan gum films
WANG Zhiqiang,WANG Yuanzhe,WANG Jingyi,WANG Guiying
DOI: https://doi.org/10.13995/j.cnki.11-1802/ts.031560
2023-01-01
Abstract:To develop new food packaging materials, gellan gum was used as film-forming base with glycerol, propylene glycol, and polyethylene glycol 400 as plasticizers and biodegradable packaging films were prepared by casting method. The microstructure, stability, mechanical properties, light transmission, water vapor, and oxygen permeability of the films was investigated. Compatibility analyzed between the three plasticizers and gellan gum by infrared spectroscopy, X-ray diffraction, and electron microscope scanning showed that glycerol＞ propylene glycol＞polyethylene glycol 400. Thermogravimetric analysis showed that the three base films exhibited good and uniform thermal stability in the temperature range of 0-100 ℃ and propylene glycol＞glycerol＞polyethylene glycol 400. The physical performance test analysis showed that the addition of the three plasticizers increased the thickness, elongation at break, tensile strength, water vapor, and oxygen permeability rates of the base film, and reduced the light transmission performance. When the film was prepared by adding 40% glycerol（mass fraction, gellan gum base）, the maximum tensile strength was 32.46 MPa, the maximum elongation at break was 8.33%, and the maximum oxygen permeability rate was 2.11 cm~3·mm/（m~2·d·atm）, the maximum water vapor transmission rate was 2.45×10 -10 g/（m·s·Pa）, and the maximum light transmission rate was 91.8%, which met the performance requirements of packaging films. These results indicate a theoretical basis for the preparation and application of new degradable packaging films.