Abstract:The hot deformation behavior of TZM-1.0 wt% ZrO 2 alloy in the temperature range of 1000–1600 °C and strain rate range of 0.005–1 s −1 was studied by hot compression method. The constitutive equation and hot working diagram were established, and the microstructure evolution was emphatically analyzed by SEM and EBSD. The results indicate that the flow stress decreases with the increase of temperature and the decrease of strain rate, and ZrO 2 particles can improve the stability of TZM alloy in rate-control during hot deformation. The constitutive equation accurately predicted the correlation coefficient as high as 0.9685, calculated the average activation energy Q = 426 kJ mol −1 , and obtained the best process parameters of 1150 °C–1250 °C /0.01–0.05 s −1 under 0.7 strain. The unstable zone was mainly composed of a small number of coarse grains and a large number of fine grains. The main reason for flow instability was the disharmonious deformation between coarse and fine grains during compression. The optimum hot working zone consists of more uniform equiaxed grains. However, EBSD observed that at a strain rate of 1 s −1 , the recrystallization fraction at 1600 °C was lower than 1200 °C, and the dynamic recrystallization (DRX) and texture evolution trends at 1200 °C and 1600 °C were completely different. The abnormal changes in recrystallization fraction and texture evolution at 1600 °C were due to the competition between deformed grain growth and DRX on energy storage consumption, and the effect of deformed grain growth on energy storage consumption was greater than that of DRX. At 1600 °C/1 s −1 , the growth of deformed grains was dominant, exhibiting strong texture components in the [001] direction, with〈100〉fibers as the main component and the highest peak texture strength. As the strain rate decreases, DRX dominates and weakens the texture strength, resulting in a significant decrease in fibers.

Elevated Temperature Compressive Failure Behavior of a 30vol.%zrcp/w Composite

Influence of Zrc Content on the Elevated Temperature Tensile Properties of Zrcp/W Composites

Compressive Deformation Behavior of a 30 Vol.%zrcp/w Composite at Temperatures of 1300–1600 °C

Elevated Temperature Compressive Strength and Deformation Behavior of A Zrcp Reinforced Tungsten-Matrix Composite

Flow stress behavior of 30ZrCP/W composite under high temperature compression deformation

Dislocation Behavior in ZrC Particles During Elevated Temperature Compressive Deformation of a 30 Vol.% ZrC_p/W Composite

Strength properties and fracture behavior of ZrC particle-reinforced tungsten composite

Elevated temperature fracture behavior of ZrC particle-reinforced tungsten matrix composite

High temperature tensile properties of 30 vol. pct ZrCp/W composite

Microstructures and Mechanical Properties of ZrCP/W Composites at Room Temperature

Elevated temperature strength of a 20 vol % ZrCp/W composite

The Mechanical and Thermophysical Properties of ZrC/W Composites at Elevated Temperature

Microstructure and mechanical properties of 20Wf/30ZrCp/W composite

Crystal Defects Responsible for Mechanical Behaviors of a WC-Co Composite at Room and High Temperatures - a Simulation Study.

Effect of ZrC Particle Size on Microstructure and Room Temperature Mechanical Properties of ZrCp/W Composites

Microstructure and high temperature mechanical properties of hot-pressed ZrB2-based composites

High Temperature Electrical Resistivities of Zrc Particle-Reinforced Tungsten-Matrix Composites

Deformation Behavior and Microstructure Evolution Mechanism of 5vol.% (tibw + TiCp)/Ti Composites During Isothermal Compression

Evaluation of TZM/ZrCp-W Joint Brazed with Ti-35Ni Filler: Microstructure and Mechanical Properties

Deformation behavior and microstructure evolution of TZM alloy with 1.0 wt%ZrO 2 under high temperature compression

Thermal shock and ablation behavior of ZrCP/W composite by the motor test