Abstract:The structural properties of the Na2CsC60 fulleride have been studied by synchrotron X-ray powder diffraction at both ambient and elevated pressures. Complementary neutron diffraction measurements at high pressure were also performed. We find no evidence for a monomer → polymer phase transition on cooling at ambient pressure, despite the adopted slow cooling procedures, with the structure remaining strictly cubic, even after prolonged standing at 200 K. The pressure dependence of the structure of solid Na2CsC60 at ambient temperature was followed up to 0.56 GPa by neutron diffraction and up to 8.63 GPa by synchrotron X-ray diffraction. At ambient pressure, the structure is primitive cubic with a=14.1329(3) Å (space group Pa3). When a pressure of 0.76GPa is reached, an incomplete phase transition to a low-symmetry structure, accompanied by a large volume decrease (2.7(1)%), is encountered. This phase was characterized as monoclinic with a=13.745(5) Å, b=14.224(6) Å, c=9.408(3) Å, and β=133.71(1)° (space group P21/a), isostructural with the low-temperature polymer phase of Na2RbC60. The cubic and polymeric phases of Na2CsC60 coexist up to 0.90 GPa. The pressure evolution of the monoclinic lattice constants a, b, and c to 8.63 GPa reveals the presence of substantial anisotropy in the compressibility along the three axes. The structure is least compressible along the c axis, which defines the polymeric C–C bridged fulleride chains and is most compressible along the interchain b direction.

Crystal Structure, Bonding, and Phase Transition of the Superconducting Na2CsC60 Fulleride.

Pressure and Temperature Evolution of the Structure of the Superconducting Na2CsC60 Fulleride

Structure and Properties of NaxCsyC60 Superconductors

NMR Studies on Orientational Ordering Phase Transition in Na2CsC60

Structure and superconductivity of C60 fullerides

High Pressure Polymerization of the Li-Intercalated Fulleride Li3csc60

Electronic States and Superconductivity in Alkali-Intercalated Fullerides:13C-NMR Study in Na2RbC60, Na2CsC60, K3C60, K2RbC60, K2CsC60, KRbCsC60, Rb2CsC60and RbCs2C60

Instability of Pa$\overline 3$ Cs$_{3}$C$_{60}$ at ambient pressure and superconducting state of the FCC phase

Orientational Disorder of C60 in Li2CsC60.

Superconductivity of Fullerenes Doped with Binary Alkali-Metals

Visualizing Molecular Orientational Ordering and Electronic Structure in CsnC60 Fulleride Films

NMR Studies of Superconductingna2ac60(a…

Structural And Electronic Properties Of The Noncubic Superconducting Fullerides A ' C-4(60) (A '= Ba, Sr)

Clathrate Structure of Fullerite C60

Close-Packed C<sub>70</sub><sup>3-</sup>Phases − Synthesis, Structure, and Electronic Properties

Neutron diffraction study of the polymeric structure of

Superconductivity in Sodium-and Lithium-Containing Alkali-Metal Fullerides

Close-Packed C703- Phases − Synthesis, Structure, and Electronic Properties

Superconductivity of li2mc6oand na2mc60fullerides

Superconductivity of Li<sub>2</sub>MC<sub>60</sub> and Na<sub>2</sub>MC<sub>60</sub> Fullerides

Pressure Dependence of Superconductivity in Simple-Cubicna2csc60