Abstract:Ultrathin microporous polymer films are pertinent to the development and further spread of nanotechnology with very promising potential applications in molecular separations, sensors, catalysis, or batteries. Here, we report high-pressure CO2 sorption in ultrathin films of several chemically different polymers of intrinsic microporosity (PIMs), including the prototypical PIM-1. Films with thicknesses down to 7 nm were studied using interference-enhanced in situ spectroscopic ellipsometry. It was found that all PIMs swell much more than non-microporous polystyrene and other high-performance glassy polymers reported previously. Furthermore, chemical modifications of the parent PIM-1 strongly affected the swelling magnitude. By investigating the behavior of relative refractive index, nrel, it was possible to study the interplay between micropores filling and matrix expansion. Remarkably, all studied PIMs showed a maximum in nrel at swelling of 2-2.5% indicating a threshold point above which the dissolution in the dense matrix started to dominate over sorption in the micropores. At pressures above 25 bar, all PIMs significantly plasticized in compressed CO2 and for the ones with the highest affinity to the penetrant, a liquidlike mixing typical for rubbery polymers was observed. Reduction of film thickness below 100 nm revealed pronounced nanoconfinement effects and resulted in a large swelling enhancement and a quick loss of the ultrarigid character. On the basis of the partial molar volumes of the dissolved CO2, the effective reduction of the Tg was estimated to be ∼200 °C going from 128 to 7 nm films.

Low-Pressure Co2 Sorption In Ammonium-Based Poly(Ionic Liquid)S

Poly(ionic Liquid)s As New Materials for CO2 Absorption

Preparation and Co2 Sorption/Desorption of N-(3-Aminopropyl) Aminoethyl Tributylphosphonium Amino Acid Salt Ionic Liquids Supported into Porous Silica Particles

Enhanced Co2 Absorption Of Poly(Ionic Liquid)S

Isothermal Carbon Dioxide Sorption in Poly(ionic Liquid)s

Carbon Dioxide Solubility in Polymerized Ionic Liquids Containing Ammonium and Imidazolium Cations from Magnetic Suspension Balance: P[VBTMA][BF4] and P[VBMI][BF4]

Porosity and hydrophilicity modulated quaternary ammonium-based sorbents for CO<sub>2</sub> capture

Poly(ionic liquid)s: a new material with enhanced and fast CO2 absorption

Evaluating Biocompatible Amino Acid-Based Poly(ionic liquid)s for CO2 Absorption

Absorption of Polymers of Ammonium-Based Ionic Liquid Monomers

Amine-functionalized amino acid-based ionic liquids as efficient and high-capacity absorbents for CO(2)

Theoretical studies on CO2 capture behavior of quaternary ammonium-based polymeric ionic liquids.

Porous Polymer Supported Amino Functionalized Ionic Liquid for Effective CO2 Capture

Carbon dioxide adsorption onto modified polyvinyl chloride with ionic liquid

Efficient Selective CO2 Composite Sorbent from Amino Acid Ionic Liquids and Silica Gel: 2H NMR Spectroscopy Provides Insight on the CO2-Binding Mechanism and in-Pore Microscopic Viscosity

Atom Transfer Radical Polymerization of Styrenic Ionic Liquid Monomers and Carbon Dioxide Absorption of the Polymerized Ionic Liquids

Click-based porous cationic polymers for enhanced carbon dioxide capture

Sponge-like Quaternary Ammonium-Based Poly(ionic Liquid)s for High CO2 Capture and Efficient Cycloaddition under Mild Conditions

Efficient selective CO2 composite sorbent from amino acid ionic liquids and silica gel: Insight on the CO2‐binding mechanism and in‐pore microscopic viscosity by means of 2H NMR

Tailored Carbon Dioxide Capacity in Carboxylate-Based Ionic Liquids†

High-Pressure CO2 Sorption in Polymers of Intrinsic Microporosity under Ultrathin Film Confinement