Preparation and Biological Evaluation of Nano-hydroxyapatite/Collagen composites
Xiao-Yan LIN,Hong-Song FAN,Xu-Dong LI,Min TANG,Ling-Li ZHANG,Yan-Fei TAN,Jin-Rui XU,Xing-Dong ZHANG
DOI: https://doi.org/10.3969/j.issn.0258-8021.2006.01.013
2006-01-01
Abstract:The homogeneous dispersion of nanohydroxyapatite treated by hydrothermal method was added into neutral collagen sol to prepare composite sol at low temperature,the composite gel of hydroxyapatite/ collagen was formed through self-assembly by adjusting the system temperature.After washed, freeze-dried,the hydroxyapatite/collagen composites were investigated by XRD,FTIR,and TEM respetively.The results showed that the average size of hydroxyapatite crystals was 16nm×40nm.The composites were similar to natural bone to some extent in crystallite phase composition,crystallite size of hydroxyapatite and micro-structure of collagen fibril.Biocompatibility of the composites was evaluated by mouse micronucleus test,guinea pig sensitization test,in vitro cytotoxicity test respec-tively.The percentage of micronucleated polychromatic erythrocytes of mice bone marrow cells,was 1.6±0.9,which was not significant different from the negative control,but significant different from the positive control.The results of guinea pig maximization tests showed that the composite did not show any signs of sensitization.The composite did not exhibit cytotoxicity in the filter diffusion tests.Histological findings of the composites implanted in rabbit bone showed that new bone formation occurred in the boundary layer between the composite and recipient bone after 4 weeks.Formation of new bone proceeded with time after the operation,newly formed bones in a lager quantitative were found in the region around the composite after 12 weeks.After implanted subcutaneously in rat 44 weeks,the composite degraded into small fragments and fiber tissues grew into the regions of degraded composites.Experimental results demonstrated that the nanohydroxyapatite/collagen composites were biodegradable and able to induce formation of new bone.No chromosome mutagenesis,cytotocixity and sensitization on skins caused were found in the evaluation experiments.The composites have excellent biocompatibility and expected to be used in bone repair.