Interfilamentary coupling properties of Bi2223/Ag tapes with oxide barriers subjected to AC perpendicular magnetic field

Ryoji Inada,Yuichi Nakamura,Akio Oota,Chengshan Li,Pingxiang Zhang

DOI: https://doi.org/10.1016/j.physc.2009.09.007

2010-01-01

Abstract:In this paper, we fabricated Bi2223 tapes with interfilamentary oxide barriers and evaluated interfilamentary coupling properties under an AC perpendicular magnetic field at 77K. To avoid the side effect on Bi2223 phase formation during sintering process, SrZrO3 was selected for barrier materials. Moreover, 20wt.% Bi2212 was mixed with SrZrO3 to improve its ductility for cold working. Monocore Ag-sheathed rods were coated by the oxide barriers with slurry before stacking with a honeycomb structure. By twisting the filament with twist pitch length below 10mm and introducing interfilamentary barriers, the coupling frequency (fc) under an AC perpendicular field, which is inversely proportional to the decay time constant (τc) of coupling current, exceeded 100Hz. At perpendicular field amplitude above full-penetration field, the magnetization losses of the twisted barrier tape were reduced by 30–40% around power-grid frequency, compared with analytical values for fully-coupled filaments. However, the loss values were still considerably higher than the prediction of the hysteresis loss (Qh) for the completely decoupled filaments. From the frequency dependence of losses, it was suggested that the loss reduction of twisted barrier tape around power-grid frequency were limited by not only the contribution of coupling current loss (Qc) but also the insufficient Qh reduction due to the presence of physical connection among the filaments positioned near the center of a tape section.