Aluminum borate whiskers modified by silane coupling agent to enhance bending force of PMMA
ZHANG Xiu-yin,WU Wen-sheng,TIAN Ai-feng,LIU Yi-rong,ZHU Ming-yi
2009-01-01
Abstract:Objective To study the enhancing effects of the bending strength of PMMA after aluminum borate whiskers modified by silane coupling agent.Methods The aluminum borate whiskers were surface-treated by silane coupling agent Z-6030 at 1.0%,2.0%,3.0%,4.0%,respectively(ratio),while the untreated ones were considered as the control group.Then the five groups of surface-treated whisker were mixed into the resin matrix with the 10 percent filling and five groups of whisker /PMMA composite material were synthesized,and then they were made to the standard size samples.At last,the three-point bending test was made and the fracture surfaces were observed by electron microscopy(SEM).Results The bending strengths of the five groups were 67.59±5.35,72.96±4.20,75.52±4.89,71.26±5.94 and(68.25±3.43)MPa,respectively.When the amount of silane coupling agent for the quality of aluminum borate whisker was 2.0 percent,the bending strength was maximum.Analyzing the results of the 5 groups by comparing the average two by two(Tukey test),it was indicated that the bending strength of the five groups was not significantly different(P>0.05).The SEM pictures of the groups treated by 2.0% silane coupling agent showed the combination of resin and whisker has been very good.Conclusion Silane coupling agent can enhance the strength between aluminum borate whiskers and PMMA interface,but different amounts will have different impact on the bending strength of whisker /PMMA composite material,as too much or too little will cause the interface strength to decline,and it will show the declined bending strength in macro.For this experiment,when the amount of silane coupling agent occupied the aluminum borate whisker's mass fraction of 2%,the enhancing effect was the best,and it showed the largest bending strength of composite material.