Preparation of MoS2 spherical and rod-like particles by an extraction-solvothermal method
Jifen Wu,Xun Fu,Xiaodong Zhou,Zhengshui Hu
DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.z2.027
2007-01-01
Rare Metal Materials and Engineering
Abstract:Molybdenum disulfide hollow spherical and rod-like particles of MoS2 have been successfully prepared by a simple low temperature method, Le extraction-solvothermal method. MoS42- ions were extracted into gasoline by extractant trioctylamine TOA After phase separation, the extracted organic phase was treated with N(2)H4 center dot H2O in autoclave at 190 degrees C for 24 h. By changing the amount of reducing agent, hollow sphere-like MoS2 with diameters of about 30 nm and small pieces were obtained respectively. Calcining the MoS2 piece at 600 degrees C for 2h under Ar flow, rods with diameters of 100 nm(-1) gm, length of 5-20 gm were obtained. The samples were characterized by XPS, TEM, XRD and the wear-resistant properties of as-prepared hollow sphere-like MoS2 were tested. Key words: extraction-solvothermal method; trioctylarnine; nanomaterial; molybdenum disulfide; wear-resistant property
What problem does this paper attempt to address?