Density functional theory study of sulfur tolerance of CO adsorption and dissociation on Rh–Ni binary metals

Kyungtae Lee,Chunshan Song,Michael J. Janik

DOI: https://doi.org/10.1016/j.apcata.2010.09.015

2010-01-01

Abstract:The effect of Ni addition to improve the sulfur tolerance of a Rh catalyst for CO dissociation was studied using density functional theory (DFT) methods. Adsorption and dissociation were considered over the (111) surfaces of binary Rh1Ni2 and Rh2Ni1 metals with comparison to pure Rh and Ni surfaces. Sulfur adsorption on the Rh1Ni2(111) surface is 0.21eV more endothermic than on the Rh(111) surface, suggesting that a Rh1Ni2 bimetallic catalyst has a higher sulfur tolerance than pure Rh catalysts due to a lower surface coverage of the sulfur poison. To compare catalytic activity in the presence of adsorbed sulfur, the CO dissociation rates over the binary and pure metals were calculated with 1/9 sulfur coverage. CO dissociation is fastest on the pure Rh surface under sulfur-free conditions, whereas among sulfur poisoned surfaces, the Rh1Ni2 surface shows the fastest CO dissociation rate. The CO dissociation barrier on Rh1Ni2 is destabilized less by a S coadsorbate than for the other metals. The addition of Ni atoms to a Rh catalyst improves the sulfur tolerance of the catalyst for CO dissociation by minimizing the repulsion between the adsorbed S atom and the CO dissociation transition state, as evidenced through a projected density of states analysis. The Rh1Ni2(221) stepped surface also shows a lower activation barrier and higher CO dissociation rate in the presence of sulfur than the Rh(221) stepped surface.