Abstract:Successive ion layer adsorption and reaction (SILAR) originally developed for the deposition of thin films on solid substrates from solution baths is introduced as a technique for the growth of high-quality core/shell nanocrystals of compound semiconductors. The growth of the shell was designed to grow one monolayer at a time by alternating injections of air-stable and inexpensive cationic and anionic precursors into the reaction mixture with core nanocrystals. The principles of SILAR were demonstrated by the CdSe/CdS core/shell model system using its shell-thickness-dependent optical spectra as the probes with CdO and elemental S as the precursors. For this reaction system, a relatively high temperature, about 220-240 degrees C, was found to be essential for SILAR to fully occur. The synthesis can be readily performed on a multigram scale. The size distribution of the core/shell nanocrystals was maintained even after five monolayers of CdS shell (equivalent to about 10 times volume increase for a 3.5 nm CdSe nanocrystal) were grown onto the core nanocrystals. The epitaxial growth of the core/shell structures was verified by optical spectroscopy, TEM, XRD, and XPS. The photoluminescence quantum yield (PL QY) of the as-prepared CdSe/CdS core/shell nanocrystals ranged from 20% to 40%, and the PL full-width at half-maximum (fwhm) was maintained between 23 and 26 nm, even for those nanocrystals for which the UV-vis and PL peaks red-shifted by about 50 nm from that of the core nanocrystals. Several types of brightening phenomena were observed, some of which can further boost the PL QY of the core/shell nanocrystals. The CdSe/CdS core/shell nanocrystals were found to be superior in comparison to the highly luminescent CdSe plain core nanocrystals. The SILAR technique reported here can also be used for the growth of complex colloidal semiconductor nanostructures, such as quantum shells and colloidal quantum wells.

Mesoporous Silica Spheres As Microreactors for Performing CdS Nanocrystal Synthesis

Synthesis of CdSe Nanoparticles into the Pores of Mesoporous Silica Microspheres

Synthesis of ZnS Nanoparticles into the Pore of Mesoporous Silica Spheres

Synthesis of Cds Hollow/Solid Nanospheres and Their Chain-Structures by Membrane Technique

Facile synthesis of high-quality nano-sized CdS hollow spheres and their application in electrogenerated chemiluminescence sensing

CdS@SiO2 Nanoparticles Synthesized from Polyoxyethylene (10) Tertoctylphenyl Ether Based Reverse Microemulsion

A Simple Approach to Fabricate CdS-SiO2 Hybrid Microspheres by Producing CdS Nanoparticles on the Surface of Thiolated SiO2 Microspheres

Synthesis, Characterization and Optical Properties of CdS Nanoparticles Confined in SBA-15

Confined Growth of CuO, NiO, and Co3O4 Nanocrystals in Mesoporous Silica (MS) Spheres

Confined Growth of CdSe Quantum Dots in Colloidal Mesoporous Silica for Multifunctional Nanostructures

Fabrication of Hierarchical CdS Microspheres Assembled by Nanowires: Solid State Electro-Chemiluminescence in H2O2 Solution

In Situ Fabrication of Mesoporous CdS Nanoparticles in Microemulsion by Gamma Ray Irradiation

Silica Coating Of Water-Soluble Cdte/Cds Core-Shell Nanocrystals By Microemulsion Method

Preparation of CdSe/CdS/SiO2 nanospheres and their luminescent properties

Synthesis of CdS nanocrystals in polymer-impregnated sol-gel silica matrix

Controlled synthesis and properties of CdS quasi-nanospheres with artificial active membrane as template

Low Temperature Hydrothermal Synthesis of CdS Submicro- and Microspheres Self-Assembled from Nanoparticles

Large-scale Synthesis of Nearly Monodisperse CdSe/CdS Core/shell Nanocrystals Using Air-Stable Reagents Via Successive Ion Layer Adsorption and Reaction.

CdS-Nanoparticle/Polymer Composite Shells Grown on Silica Nanospheres by Atom-Transfer Radical Polymerization

Synthesis and Photoluminescence Properties of CdS Hollow Nanospheres by Chemical Vapor Deposition

A Facile Synthesis of Monodispersed Mesoporous Silica Nanospheres with Pm3n Structure