Abstract:Single-stage hydrotreating (HDT) of loblolly pine biocrude produced from catalytic pyrolysis was conducted to gain insight to HDT performance in terms of product yields, liquid product quality, and hydrogen consumption. Tests were performed with a sulfided HDT catalyst at three different conditions. The longest continuous time onstream operation (365 h) was achieved at an average bed temperature of 290 degrees C, 138 bar pressure, H2/oil ratio of 3300 Nl l(-1), and a liquid hourly space velocity (LHSV) of 0.25 h(-1). The average carbon yield of the HDT liquids were 77%, 83%, and 89% for experiments 1, 2, and 3, respectively. Also, the biocrude carbon that ended up in the gas phase varied between 4.3% and 8.9%. The carbon in the aqueous phase fraction was negligible-less than 0.5% of the biocrude carbon. The average hydrogen consumed ranged from 0.04 g to 0.07 g per 1 g of dry biocrude. The highest carbon content measured for the HDT liquid products from all three experiments was 87.13 wt% and the lowest was 79.03 wt%. GC-MS analysis suggests that the HDT product with oxygen content less than 5 wt% contained mainly naphthenic hydrocarbons. On the other hand, HDT products with oxygen content greater than 5 wt% contained a higher concentration of simple phenols and aromatic hydrocarbons (mono-and poly-). Catalyst deactivation was evident in the quality of the HDT liquid collected over time; the density and viscosity increased, the H/C ratio and carbon contents decreased; also, the gasoline fraction decreased while the gas oil fraction increased. The results from this work suggest that HDT of biocrude produced by catalytic biomass pyrolysis can be successfully upgraded into hydrocarbon liquid fuels without a stabilization step.

Catalytic Degradation of High Density Polyethylene and Polypropylene into Liquid Fuel in A Powder-Particle Fluidized Bed

Catalytic Hydrogenolysis of Plastic to Liquid Hydrocarbons over a Nickel-Based Catalyst

Catalytic Degradation of High-Density Polyethylene over A Clay Catalyst Compared with Other Catalysts

Polyethylene terephthalate conversion into liquid fuel by its co-pyrolysis with low- and high-density polyethylene employing scrape aluminium as catalyst

Polyolefin Pyrolysis in Multilayer Fluidized Beds: An Innovative Approach to Obtain Valuable Alternative Fuels

CONVERSION OF WASTE POLYPROPILENE (PP) USING THE ZEOLITE Ni/ZSM-5 TO LIQUID FUEL

Integration of catalytic fast pyrolysis and hydroprocessing: a pathway to refinery intermediates and “drop-in” fuels from biomass

Catalytic pyrolysis of polyolefin waste into valuable hydrocarbons over reused catalyst from refinery FCC units

Mechanistic Understanding of Efficient Polyethylene Hydrocracking over Two-Dimensional Platinum-Anchored Tungsten Trioxide.

Catalytic hydrogenolysis of polypropylene and polyethylene mixtures: Effect of temperature on liquid alkane components

Catalytic Pyrolysis of Polyethylene and Polypropylene Over Y Zeolite

Integrating continuous-stirred microwave pyrolysis with ex-situ catalytic upgrading for linear low-density polyethylene conversion: Effects of parameter conditions

Polyethylene upcycling to fuels: Narrowing the carbon number distribution in n-alkanes by tandem hydropyrolysis/hydrocracking

Efficient Pyrolysis of Low-Density Polyethylene for Regulatable Oil and Gas Products by ZSM-5, HY and MCM-41 Catalysts

Enhanced Oil Yield by Catalytic Pyrolysis of Thermoplastics Using Cost-Effective Spent FCC and BaCO3 and Its Valorization to Gasoline and Diesel Grade Fuel via Fractionation

Catalytic co‐pyrolysis of low‐density polyethylene (LDPE) and lignin for jet fuel range hydrocarbons over activated carbon catalyst

Analysis of liquid products and mechanism of thermal/catalytic pyrolysis of HDPE

Microwave-assisted pyrolysis of low-density polyethylene (LDPE)to value-added products over HY, HZSM-5 and Hβ catalyst

Two-stage thermocatalytic conversion of waste XLPE to diesel-like fuel

Influence of retention time and catalyst concentrations on catalytic pyrolysis yields of polyethylene and polystyrene

THERMAL CATALYTIC PYROLYSIS PROCESS STUDIES FOR POST CONSUMER POLYETHYLENE WASTE CONVERSION