High-pressure synthesis, structure and properties of new ternary pnictides La3TiX5 (X = P, As)
Lei Duan,Jun Zhang,Xiancheng Wang,Jianfa Zhao,Lipeng Cao,Wenmin Li,Zheng Deng,Runze Yu,Zhi Li,Changqing Jin
DOI: https://doi.org/10.1016/j.jallcom.2020.154697
IF: 6.2
2020-08-01
Journal of Alloys and Compounds
Abstract:The new ternary pnictides La3TiX 5 (X = P, As) and the solid solutions of La3Ti(Sb1-x As x )5 (x = 0–1) and La3Ti(As1-y P y )5 (y = 0–1) were synthesized under high pressure and high temperature conditions. The crystal structure of La3TiX 5 (X = P, As) was determined from the X-ray powder diffraction data. These compounds crystallize in a hexagonal Hf5Sn3Cu-anti type structure with the space group P63/mcm and lattice parameters a = 8.7927 Å and c = 5.7643 Å for La3TiP5, and a = 9.0267 Å and c = 5.9071 Å for La3TiAs5, in which the face-sharing TiX 6 octahedral chains running along the c axis are separated by La3+ in the interstice sites with a distance about 9 Å, presenting a strong one-dimensional crystal structure. Physical properties measurements indicate La3TiX 5 (X = P, As) are Pauli paramagnetic metals. The calculations reveal that La3+ ions are not perfectly ionic owing to the non-negligible contributions of La to the density of state (DOS) at the Fermi level and bridge the X atoms between the chains, which make the samples to be 3-dimensional metals. What’s more, the change of X in La3TiX 5 from Sb to P increases the ionicity of La3+ and thus decreases the electron hopping between the conducting chains.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering