Growth and Low-temperature Raman Spectra Study of Ca0.4Ba0.6Nb2O6 Crystal

Na-na ZHANG,Shu-juan HAN,Wen-lan GAO,Huai-jin ZHANG,Ji-yang WANG
2011-01-01
Abstract:The Ca0.4Ba0.6Nb2O6 crystal was grown by Czochralski method.The stability of crystal structure of Ca0.4Ba0.6Nb2O6 at low temperature 25-260 K was investigated by polarized Raman spectrum.The results indicated that as the temperature decreasing,the internal ν5 mode of NbO6 increases more unsymmetric,and the wavenumbers of lower-ν5 mode and the width of higher-ν5 mode obtained from Gauss+Lor Amp fitting show obvious variation at 70-100 K,which indicates the possibility of a structure transformation.Meanwhile,the temperature dependence of ratios of external modes under x(zz)x and x(zy)x polarizations was discussed,which also show abnornality at this temperature range.At last,the effect of population factor on Raman intensity and the experiment result was simply discussed.