Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Ce–Zr–Sr ternary mixed oxides structural characteristics and oxygen storage capacity

CeO2–CoOx mixed oxides: Structural characteristics and dynamic storage/release capacity

Structure and Oxygen Storage Capacity of Pr-doped Ce0.26Zr0.74O2 Mixed Oxides

Effects of Fe-doping of Ceria-Based Materials on Their Microstructural and Dynamic Oxygen Storage and Release Properties

Modification of CeO2–ZrO2 Mixed Oxides by Coprecipitated/impregnated Sr: Effect on the Microstructure and Oxygen Storage Capacity

Effect of Yttrium Doping on Oxygen Storage Capacity of Ce_(0.33)Zr_(0.67)O_2

Effects of Ni-Doping of Ceria-Based Materials on Their Micro-Structures and Dynamic Oxygen Storage and Release Behaviors

Structure Properties and OSC Performance of Pr-Ce-Zr Mixed Oxides

Enhanced Thermal Stability and Oxygen Storage Capacity for CexZr1-xO2 (x = 0.4−0.6) Solid Solutions by Hydrothermally Homogenous Doping of Trivalent Rare Earths

Effect of Manganese Doping on Oxygen Storage Capacity of Ceria-Zirconia Mixed Oxides

Influence of neodymia doping on the oxygen storage capacity of CeO_2-ZrO_2 mixed oxides

Improvement of the Homogeneity and Oxygen Storage Capability of Ce1-xZrxO2-δ by Co-Doping: A First-Principles Study

Influence of neodymia doping on the oxygen storage capacity of CeO2-ZrO2 mixed oxides

STUDY ON PREPARATION AND OXYGEN STORAGE CAPACITY OF CeO2-ZrO2 SOLID SOLUTION

Preparation and Characterization of CeO<sub>2</sub>-based Oxygen Storage Materials

Study The Structure And Texture Of Storage Oxygen Material Process

Preparation and property investigation of CeO2–ZrO2–Al2O3 oxygen-storage compounds

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Effect of CeO2 Addition on the Structure and Dielectric Properties of BaxSr1-xTiO3-Based Glass Ceramics

Preparation and properties of low cerium content Ce-Zr-Y oxygen storage material with high thermal stability and high specific surface area

High Performance Ce_(0.35)Zr_(0.55)Y_(0.1)O_(1.95) Rare Earth Oxygen Storage Material