DEGRADATION OF BASIC VIOLET BY ELECTROGENERATED H2O2-TiO2/UV

Jian-zhang FANG,Yu-ying PU,Jin-yun LIAO,Hao LI,Feng PENG
DOI: https://doi.org/10.3969/j.issn.1000-5463.2006.03.014
2006-01-01
Abstract:The degradation of basic violet by electrogenerated H_2O_2-TiO_2/UV system was investigated in this paper.H_2O_2 was continuously supplied to UV/TiO_2 system by electrochemical reduction of O_2 on graphite cathode to enhance photocatalytic performance.It was observed that pH value had some influence on degradation of basic violet,and degradation rate of basic violet was the fastest in alkaline solution and the slowest in neutral solution.Increasing current density from 5.0 mA·cm~-2 to 10.0 mA·cm~-2 resulted in a pronounced increase in degradation ratio,but a further increase in current density had little influence on basic violet removal.Both PO_4~3-and SO_4~2-impeded photocatalytic degradation of basic violet,while Cl~-could improve the treatment efficiency.The degradation and COD removal of basic violet in electrogenerated H_2O_2-TiO_2/UV system was found to be much more efficient than the sum of those by sole electrolysis and photocatalysis alone,indicating a significant synergetic effect between electrolysis and photocatalysis.It was also found that the decomposition and COD removal of basic violet was well fitted by the first order kinetics,and the first order reaction rate constant were 3.109×10~-2 min~-1 and 1.033×10~-2 min~-1,respectively.
What problem does this paper attempt to address?