Electrochemical performance and structural stability of layered Li–Ni–Co–Mn oxide cathode materials in different voltage ranges
Zhiguo Wang,Huang Luo,Hui Liu,Fangfang Wu,Chun Zhang,Zhixing Wang,Peng Yu
DOI: https://doi.org/10.1016/j.ceramint.2020.11.216
IF: 5.532
2021-03-01
Ceramics International
Abstract:<p>In this study, layered Li–Ni–Co–Mn oxide (LiNi<sub>1-<em>x</em>-<em>y</em></sub>Co<sub><em>x</em></sub>Mn<sub><em>y</em></sub>O<sub>2</sub>) cathode materials with different transition metal compositions (LiNi<sub>1/3</sub>Co<sub>1/3</sub>Mn<sub>1/3</sub>O<sub>2</sub>, LiNi<sub>0.5</sub>Co<sub>0.2</sub>Mn<sub>0.3</sub>O<sub>2</sub>, and LiNi<sub>0.8</sub>Co<sub>0.1</sub>Mn<sub>0.1</sub>O<sub>2</sub>) are synthesized by a simple mixing process and solid-state reaction at a high temperature. The samples show a typical hexagonal α–NaFeO<sub>2</sub> structure with a single phase and predominantly spherical morphology with a homogeneous particle size distribution. The electrochemical properties of the samples are investigated in different voltage ranges by galvanostatic charge/discharge tests. The results reveal that the capacity increases with increasing the charging cutoff voltage by 0.1 V for all the samples. In addition, the LiNi<sub>1/3</sub>Co<sub>1/3</sub>Mn<sub>1/3</sub>O<sub>2</sub>, LiNi<sub>0.5</sub>Co<sub>0.2</sub>Mn<sub>0.3</sub>O<sub>2</sub> and LiNi<sub>0.8</sub>Co<sub>0.1</sub>Mn<sub>0.1</sub>O<sub>2</sub> samples deliver initial discharge capacities of 161.0, 170.8, and 202.3 mAh g<sup>−1</sup>, respectively, at a 0.1 C rate with the voltage ranging from 3.0 to 4.3 V, which increase by 23.4%, 18.8%, and 8.2%, respectively, with the increase in the charging cutoff voltage from 4.3 to 4.6 V. Furthermore, compared with LiCoO<sub>2</sub>, the samples exhibit a relatively superior cycling performance with an increase of the charging cutoff voltage. Cyclic voltammetry tests reveal that the redox process at approximately 4.5–4.6 V corresponds to Co<sup>3+</sup>/Co<sup>4+</sup>, and that at approximately 3.6–3.8 V corresponds to Ni<sup>2+</sup>/Ni<sup>4+</sup>. X-ray diffraction measurements confirm the reversible phase transition and excellent structural stability of the LiNi<sub>1-<em>x</em>-<em>y</em></sub>Co<sub><em>x</em></sub>Mn<sub><em>y</em></sub>O<sub>2</sub> materials against prolonged cycling.</p>
materials science, ceramics