Repairing of Articular Cartilage Defect of Rabbits with PLGA Composite with Collagen Type Ⅱ and Growth Factors
XIONG Gao-xin,ZHA Zhen-gang,TAN Wen-cheng,WU Hao,LIN Hong-sheng,XIA Ji-sheng,HUANG Xin-pei,TU Mei,ZHANG Jia-qing,LI Jie-ruo
DOI: https://doi.org/10.13471/j.cnki.j.sun.yat-sen.univ(med.sci).2010.0090
2010-01-01
Abstract:【Objective】To observe the condition of constructing the tissue engineered osteochondral composite through bone marrow stem cells(BMSCs)cultured on the poly-lactide-co-glycolic acid(PLGA),which is modified with collagen and cellular growth factors.In order to explore a new method of constructing the tissue engineered chondral composite.Then observe the effect of the composite cartilage on repairing of articular cartilage defect to rabbits.【Methods】PLGA was made by phase separation technique,composite with collagen typeⅡ,basic fibroblast growth factor and transforming growth factor-β1.The third era(P3) BMSCs were cultured on the above scaffold.Thirty-six New Zealand white rabbits were divided into experimental group,control group,blank group at random.These groups were implanted with BMSCs/growth factors and collagen-PLGA,growth factors and collagen-PLGA and collagen-PLGA into the muscle respectively.Then observe the directional differentiation and growth condition ofcells at the 4th,8th,and 12th week after the operations.Including general shape observation,HE,toluidine blue,collagen typeⅡ staining and the cells shape observation through scanning electron microscope.Sixteen New Zealand white rabbits were divided into two groups at random.The composite materials were planted into the cartilage defects of the keen of the experimental group,while the control group was left untreated.Then observe the effect of the repairing condition at the 12th week after the operation.【Results】There was cartilage-like tissue growing in experimental group in its general shape,while there was only fibrous tissue growing in control group and blank group.Various staining and scanning electron microscope observation showed:there were many cartilages and some osteoblasts in the composite of experimental group.The toluidine blue and collagen typeⅡstaining in experimental group were both positive,while in control group and blank group were negative.In the defect experiment,the defects were repaired,and the HE staining showed that articular cartilage formed and linked with the normal cartilage around.【Conclusion】PLGA modified with collagen had a good cellular compatibility.BMSCs cultured on PLGA,which was modified with collagen and cellular growth factors,could be inducted into tissue engineered osteochondral composite in rabbits.And the composite cartilage could repair articular cartilage defect of Rabbits.