Novel stable enhanced visible light photocatalytic system based on a Ag3PO4@polypyrrole core-shell Z-scheme with in-situ generated metallic Ag ohmic contacts
Xiuguo Sun,Zhe Liu,Junzhen Guo,He Li,Dongdong Wei,Zhikang Li,Na Zhou,Taolin Zhao,Gang Yu,Yanting Li
DOI: https://doi.org/10.1016/j.jpcs.2020.109572
IF: 4.383
2020-11-01
Journal of Physics and Chemistry of Solids
Abstract:<p>Maintaining the high photocatalytic activity and stability of Ag<sub>3</sub>PO<sub>4</sub> in practical applications is a still a major challenge. In this study, a series of Ag<sub>3</sub>PO<sub>4</sub>@polypyrrole (PPy) core-shell structure photocatalysts were prepared successfully by facile in-situ oxidative polymerization. A transmission electron microscopy image of the composite showed that the PPy shell with a thickness of 5–10 nm was coated tightly on the surface of the Ag<sub>3</sub>PO<sub>4</sub> particle core. X-ray diffractometer and X-ray photoelectron spectroscopy analyses demonstrated that the silver ions were reduced to metallic Ag during polymerization. Ultraviolet–visible diffuse reflectance spectra indicated that the light response range of PA-5 broadened from 300 to 630 nm. Compared with pure Ag<sub>3</sub>PO<sub>4</sub>, the composites exhibited higher photocatalytic activities and better photostability, especially Ag<sub>3</sub>PO<sub>4</sub>@PPy with a PPy content of 5 wt% (PA-5). The degradation rate of PA-5 with organic dyes exceeded 98% within 15 min under visible light irradiation. Even after five repeated reactions, PA-5 still maintained a high degradation rate of 94.98%. The degradation rate of the pure Ag<sub>3</sub>PO<sub>4</sub> decreased significantly from 94.53% to 60.33% after five cycles. Based on the experimental results, a reasonable mechanism is proposed for the Z-scheme electron-transfer photocatalytic system with metallic Ag as an ohmic contact.</p>
physics, condensed matter,chemistry, multidisciplinary