Abstract:Objective This study aimed to compare the four-point flexural strength of CAM-milled and sintered (as-sintered, AS) specimens with those of high-polished (HP) specimens using chairside polishing systems to simulate clinical surface conditions. Methods Seven full-contour zirconia CAM/CAM blanks with various yttria contents (3, 4, 5 mol%) including three high-translucent groups (5Y) were selected to prepare flexural specimens. The bend bar specimens (2.0 × 4.0 × 25.0 mm 3 ) were fabricated by using STL file and dental CAM machine with the respective zirconia blanks (98 mm φ and 10–14 mm in height). Twelve bar specimens were machined from one zirconia puck and a total of 24 specimens were prepared from each group. The pre-sintered bar specimens were sintered by using a dental zirconia furnace at 1530–1550 °C for 2 h according to the instructions. All sintered specimens were divided into two groups: as-sintered (AS) group and high-polished (HP) groups (n = 12). HP groups were subjected to polishing one surface of specimens using a three-step polishing system and finally finished with diamond polishing. After cleaning and drying, the flexural strength of all specimens was determined by a fully articulating four-point flexure fixture consisting of a 1/4-point test configuration with an inner/outer span of 10/20 mm. Statistical differences between AS and HP groups were conducted with Weibull analysis. The fractured surfaces of zirconia specimens were observed using a field emission SEM and EDS to detect failure origins. Results The mean AS flexural strength values were significantly lower than those of HP counterparts. However, Weibull moduli expressing the reliability of HP groups were generally decreased although not significantly in comparison to their AS. The fracture of the AS specimens mostly originated from extrinsic CAM-milling defects, while the HP specimens were fractured from intrinsic subsurface or volume defects including pores, large grain clusters, inclusions, and corner-located critical flaws. Two high-translucent (5Y) zirconia groups were not affected in their strength and reliability after polishing, whereas one 5Y zirconia significantly increased its strength but significantly lowered its reliability. Significance The extrinsic and intrinsic strength-limiting defects should be considered in evaluating the flexural strength and reliability of dental CAD/CAM zirconia ceramics for full-contour restorations. For the materials tested in this study, more optimized processing of blanks and milling protocols of pre-sintered zirconia blanks should be developed including post-sintering surface finishing to reduce the flaw population regulating strength and reliability which will affect the survivability of dental zirconia prostheses. Graphical Download : Download high-res image (203KB) Download : Download full-size image

[Effect of Cementation on Fracture Toughness of Chair-Side CAD/CAM Ceramic].

Comparative Study of the Influence of Heat Treatment on Fracture Resistance of Different Ceramic Materials Used for CAD/CAM Systems

Effect of surface finish and resin cement on the bond strength to CAD-CAM ceramics for interim resin-bonded prostheses

Fracture load of chairside CAD‐CAM veneers fabricated with pre‐and fully crystalized lithium disilicate ceramics

Effect of the Composition of CAD/CAM Composite Blocks on Mechanical Properties

Fracture resistance of chairside CAD‐CAM lithium disilicate occlusal veneer with various designs after mechanical aging

Effect of Surface Treatment and Cement on Fracture Load of Traditional Zirconia (3Y), Translucent Zirconia (5Y), and Lithium Disilicate Crowns

The effect of preparation design on the fracture resistance and adaptation of the CEREC ceramic endocrowns

Influence of Different Thicknesses of Monolithic Crowns Made from Different Resin-Bonded Glass Ceramic on Their Load-bearing Capacity (An in vitro Comparative Study)

A Bilayer Method for Measuring Toughness and Strength of Dental Ceramics

Influence of occlusal thickness on the fracture resistance of chairside milled lithium disilicate posterior full‐coverage single‐unit prostheses containing virgilite: A comparative in vitro study

Effect of cementation protocols on the fracture load of bilayer ceramic crowns manufactured by the Rapid Layer Technology

Impact of the Microstructure of CAD/CAM Blocks on the Bonding Strength and the Bonded Interface

Effect of repeated firing on the topographical, optical, and mechanical properties of fully crystallized lithium silicate-based ceramics

Fracture Strength of Endocrowns Fabricated From Three Different Computer-Aided Design/Computer-Aided Manufacturing Ceramic Materials: An In-Vitro Study

The Fracture Load as a Function of the Material Thickness: The Key to Computing the Strength of Monolithic All-Ceramic Materials?

The Effect of Restoration Thickness on the Fracture Resistance of 5 mol% Yttria-Containing Zirconia Crowns

Mechanical Properties of Dual-Cured Resin Luting Agents for Ceramic Restoration.

Strength-limiting damage and defects of dental CAD/CAM full-contour zirconia ceramics

Do all ceramic and composite CAD-CAM materials exhibit equal bonding properties to implant Ti-base materials? An Interfacial Fracture Toughness Study

The effect of two preparation designs on the fracture resistance and marginal adaptation of two types of ceramic crowns using CAD/CAM technology (In vitro study)