In Situ Synthesis and Structural Morphology Analysis of 3d Porous Hierarchical V2o5 Films for Transmissive-to-Black All-Solid-State Electrochromic Devices
Hongying Liu,Mengying Wang,Xu Wang,Agnieszka Pawlicka,Xungang Diao
DOI: https://doi.org/10.1016/j.cej.2024.156657
IF: 15.1
2024-01-01
Chemical Engineering Journal
Abstract:3D, porous, low-dimensional, and nanostructured V2O5 films have significant potential for application in ECDs, but their development is still in its nascency. This paper reports a facile strategy of using PEG as a structuredirecting agent and short-time heat treatments to obtain 3D, porous, and hierarchical V2O5 films comprising interpenetrating stacked ultra-long nanowire surfaces and nanorod/nanosheet mixed interiors deposited on ITOglass substrates. The mechanism of morphological transformation was studied in detail, and the analysis shows that the formation of such special structured films is a synergetic result of the guided intercalation of PEG, atomic rearrangement, Ostwald ripening, anisotropy of crystal growth, and orientation attachment mechanism. Among them, the preferred PEG addition amount of 25 % for the 350-3-V2O5 film was applied in two types of all-solidstate ECDs: one using a gel quasi-solid electrolyte and the other using a solid-film electrolyte. The 350-3-V2O5 film served as an ion storage coating and WO3 was the electrochromic layer. These devices achieved ideal reversible switching of transmissive-to-black electrochromic characteristics. Notably, the 'Integrated-Type' ECD, composed of inorganic all-solid-state films, has a large optical modulation range Delta T = 72.0 %, rapid switching responses (colouration 25.4 s and bleaching 20.8 s), and sustained electrochromic performance.