PHASE TRANSFORMATION AND STRENGTH-TOUGHNESS OF A F_(GBA)/B_G DIPHASE STEEL CONTAINING 0.02%Nb

Feng Chun,Fang Hongsheng,Bai Bingzhe,Zheng Yankang
DOI: https://doi.org/10.3724/sp.j.1037.2009.00646
IF: 1.797
2010-01-01
ACTA METALLURGICA SINICA
Abstract:In order to produce Mn-series low carbon steels using alloying elements with low cost and following the conventional production line without controlled cooling facilities and not needing special heat-treatment, Mu-series low carbon air cooling grain boundary allotriomorphic ferrite (F-GBA)/granular bainite (B-G) steels, alloying with Si-Mn-Cr, have been developed. The effect of 0.02%Nb on the phase transformation and strength-toughness of a F-GBA/B-G steel have been investigated by using Gleeble-1500D machine and hot rolling test in this paper. Two specimens with and without Nb addition were deformed by 21% at 850 degrees C and then air cooling to room temperature. For Nb free steel, the average size of F-GBA is 25 mu m in length and 10 mu m in width. The average size of intragranular ferrite is about 6-8 mu m. For F-GBA/B-G steel with 0.02%Nb, the average size of F-GBA is 10 mu m in length and 4 mu m in width. The average size of intragranular ferrite is less than 4 tan. Compared with Nb free steel, the size of bainitic ferrite and martensite/austenite (M-A) island decrease and their corresponding volume fractions increase in the FGBA/BG steel with 0.02%Nb. The experimental results indicate that the addition of 0.02%Nb increases the hardenability of the F-GBA/B-G steel, suppresses the transformation of gamma -> alpha, refines the size of grain boundary allotriomorphic ferrite, promotes the granular bainitic transformation, lowers the bainitic start temperature (B-s), and refines the granular bainite including its bainitic ferrite and M-A islands. it is suggested that the effects of structure refinement and increase of strengthening phases improve the strength of the F-GBA/B-G steel with 0.02%Nb. Compared with typical Nb free F-GBA/B-G steel after hot rolling and air cooling, it is found that the tensile strength and yield strength of the F-GBA/B-G steel with 0.02Nb% rise to 157 MPa and 97 MPa respectively. Moreover, some possible reasons of structure refinement and increase of strengthening phases induced by 0.02%Nb addition have been disscussed in this paper.
What problem does this paper attempt to address?