Abstract:Hexavalent chromium is highly toxic and carcinogenic and is not permitted for passivation of zinc in many countries. Accordingly, the development of environmentally-friendly chromium-free passivation has received increasing attention. In this paper, the preparation of Zn2+ and Al3+ doped composite passivation films on electroplated zinc surfaces using meta-aluminates as passivator was studied, and it was found that the corrosion resistance of the passivation films could be effectively improved by using EDTA. As a complexing agent, EDTA can combine with many metal ions and form stable complexes. The mechanism of the passivator and the effects of passivator concentration, temperature, time, and pH on the passivation performance were investigated. The results showed that the corrosion current density (icorr) of the meta-aluminate passivation film reinforced with EDTA decreased to 2.068 x 10-7 A/cm2, which was better than the icorr of 1.524 x 10-6 A/cm2 without EDTA reinforcement and much smaller than the icorr of 2.376 x 10-5 A/cm2 without passivation. It can be seen that the strengthening effect of EDTA results in a compact passivation film on the surface of zinc metal. Furthermore. The corrosion resistance of meta-aluminate passivation film reached or approached the level of hexavalent chromium passivation film, which contributed to the chromium-free passivation of zinc.

Trivalent Chromium Black Passivation for Zinc Deposit and Its Influence on Corrosion Resistance

Corrosion resistance of trivalent chromium black passive film on Zinc Coating

Study of Trivalent Chromium Bright Blue Passivation for Zinc Coating

Black Passivation and Corrosion Resistance of Zn-Fe Alloy Coatings

Trivalent Chromium Passivation Process for Zinc Coating

Study on Trivalent Chromium Iridescent Passivation Process for Zinc Coating

Thecomposition and corrpsion resisitance of chromium-free black passivation film on electrodeposited zinc coating

Trivalent chromium passivation for zinc coating and sealing of passivation film

Process for Trivalent Chromium Black Passivation in Cobalt-Free Sulfuric Acid System

Study on Process of Black Passivation for Zn-Fe Alloy Coating ——part I : Optimal Formular of Passivating Solution

Research Advances of Trivalent Chromium Black Passivation Process

Blue-white trivalent chromium passivation process on zinc coating with high corrosion resistance

Process for Chromium-Free Black Passivation of Zinc Coating in Silicate-Based Passivation Fluid

Process for Black Trivalent Chromium Passivation of Galvanizing Coating Obtained in Potassium Chloride Solution

Review on effects of components in passivation bath on trivalent chromium passivation of zinc coating

Causes for the Formation of Cr6+in Cr3+ Passivation Film and the Affecting Factors

Preparation of Phytic Acid/Silane Composite Passivation Coating on Hot-Dip Zinc Sheet and Its Corrosion Resistance

Improve the Performance of Cr-free Passivation Film Through Nanoelectrodeposition for Replacement of Toxic Cr 6+ Passivation in Electrogalvanizing Process

In-situ Constructing and EDTA-enhancing of Meta-Aluminate Passivation Films on Electroplated Zinc Surfaces

Corrosion Resistance Behavior of Zinc Substrate Treated with Rare Earth Salt Passivation

Research Progress of Trivalent Chrome Passivation on Zinc Plating