Preparation and characterization of nano-Li_4Ti_5O_(12)/C composite materials

Zhang Yayuan,Li Jiangang,Li Jianjun,He Xiangming

2011-01-01

Abstract:Nano-Li4Ti5O12/C composite material was prepared by using two-step solid reaction method based on effects of annealing temperature on particle size and reactivity of Li4Ti5O12,and characterized by using XRD,SEM,TG/DTA,electrochemical impedance spectra(EIS) and charge-discharge tests.The results showed that raw materials of amorphous TiO2 and Li2CO3 reacted at 600℃ to form Li2TiO3/TiO2(rutile) composite with same particle size as precursor.Annealing over 700℃ made the composite transform into Li4Ti5O12,but also increased the particle size at same time.Mixing sucrose into raw material and then one-step annealing at 800℃ produced nano-Li4Ti5O12/C but with rutile TiO2 impure phase,leading to poorer electrochemical performance.By using two-step solid reaction method including first pretreatment at 600℃ to obtain Li2TiO3/TiO2 composite,then mixing sucrose and annealing at 800℃,pure spinel nano-Li4Ti5O12/C composite with particle size of 100~200nm was prepared,which showed capacity of 167.3mAh(g-1 at 0.1C,163.1mAh(g-1 at 1C,and 96% capacity retention after 30 cycles at 1C.