The Mechanical Behavior of Water Vapor-Treated HA Coating Produced by Plasma Spraying Technique
Y. Cao,Bo Zhang,Li Ping Wang,Qiang Lin,Xu Dong Li,C. Y. Bao,Ji Yong Chen,Bang Cheng Yang,L. Yang,Xing Dong Zhang
DOI: https://doi.org/10.4028/www.scientific.net/KEM.288-289.355
2005-01-01
Key Engineering Materials
Abstract:Plasma-sprayed hydroxyapatite coating on metal substrate was prepared. Two kind of post-treatment methods were been applied to the coating, treatment in air at 650 degrees C for 30 min and treatment in water vapor at 125 degrees C with a pressure of 0.15MPa for 6 hours. XRD showed that the HA nanocrystals increased after water vapor treatment. The interfacial tensile bond strength between HA and substrate was 45.0 +/- 1.82MPa, 39.1 +/- 1.27MPa and 30.3 +/- 1.61MPa for as-received coatings, water vapor treated coatings and heated in air coatings, respectively. 3 months after implantation in dogs limbs, the push-out strength between implants and bone was 11.27 +/- 2.71MPa, 11.63 +/- 3.11MPa, 23.92 +/- 2.0 1 MPa and 18.8 +/- 1.82MPa for pure Ti implants, as-received coating implants, water vapor treated implants and heated in air implants, respectively. The results showed that the post-water vapor treated HA coating have better mechanical behavior in vitro and in vivo.