Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Concentric Sub‐micrometer‐Sized Cables Composed of Ni Nanowires and Sub‐micrometer‐Sized Fullerene Tubes

Rational Design of Coaxial MWCNTs@Si/SiOx@C Nanocomposites As Extending-Life Anode Materials for Lithium-Ion Batteries

Cnts@Sno2@C Coaxial Nanocables with Highly Reversible Lithium Storage

Strong Fiber from Uniaxial Fullerene Supramolecules Aligned with Carbon Nanotubes

Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes

Fabrication and Characterization of Ag@C Nanocables with High Aspect Ratios by Hydrothermal Process

Aligned Si3N4@SiO2coaxial Nanocables Derived from a Polymeric Precursor

Coaxial Nanocable: Silicon Carbide and Silicon Oxide Sheathed with Boron Nitride and Carbon

Synthesis and characterization of highly ordered cobalt-magnetite nanocable arrays

A Simple Large-Scale Synthesis of Coaxial Nanocables: Silicon Carbide Sheathed with Silicon Oxide

Solid–liquid–solid (SLS) growth of coaxial nanocables: silicon carbide sheathed with silicon oxide

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Transferring Self-Assembled, Nanoscale Cables into Electrical Devices.

Tailorable Coaxial Carbon Nanocables with High Storage Capabilities

Lithiation Behavior of Coaxial Hollow Nanocables of Carbon-Silicon Composite.

Synthesis and Characterization of CdS Based Sulfide Coaxial Cable and Nanotubes by Sacrificial Approach

Lightweight, Flexible, High-Performance Carbon Nanotube Cables Made by Scalable Flow Coating

Coaxial Metal Nano‐/Microcables with Isolating Sheath: Synthetic Methodology and Their Application As Interconnects

Synthesis of Copper-Core/Carbon-Sheath Nanocables by a Surfactant-Assisted Hydrothermal Reduction/Carbonization Process

Single-walled Carbon Nanotube-Based Coaxial Nanowires: Synthesis, Characterization, and Electrical Properties.

Iodine Doped Carbon Nanotube Cables Exceeding Specific Electrical Conductivity of Metals