Abstract:Using the homemade multi-walled carbon nanotubes(MWCNTs)as additive,a type of MWCNT-doped Co-Cu oxide catalyst(noted as CoiCuj-x%MWCNTs)for higher alcohol synthesis(HAS)was prepared by co-precipitation method.It was experimentally shown that MWCNT-adding amount and Co/Cu molar ratio have marked effect on the reactivity and selectivity of HAS,and that the optimal MWCNT-adding amount was 11%(mass percentage)and the optimal Co/Cu molar ratio was 3∶1.Over a Co3Cu1-11%MWCNTs catalyst under reaction conditions of 5.0 MPa,573 K,V(H2)/V(CO)/V(CO2)/V(N2)=45/45/5/5,GHSV=10000 mL/(h·g),the observed CO-conversion reached 39.1%,and the selectivity of total(C1~8)alcohols and dimethyl ether(DME)combined reached 74.3%,and the corresponding space-time-yield(STY)of C2~8 alcohols and DME combined reached 1072 mg/(h·g),the S(C2~8-alc.+DME)/S(MeOH)=17.8(C-based selectivity ratio)in the obtained total oxygenated products,a good prospect for such oxygenated products to be used as gasoline additives.The results of catalyst characterizations revealed that in the process of catalyst preparation,the formation of highly dispersed CuCo2O4 spinel crystallite phase in the oxide precursor of catalyst was utmost important for generation,through H2-reduction,of solid-solution-type bimetal CoiCuj sites catalytically active for HAS.The excellent performace of the MWCNT-promoted catalyst for adsorption and activation of H2 played important role in enhancing the reactivity and selectivity of HAS and inhibiting the side-reaction of water-gas-shift(WGS).

Preparation of MWCNTs-doped Co-Cu Oxide Catalyst for Higher Alcohol Synthesis from Syngas