Abstract:Ultra-long single-crystalline trigonal selenium submicrotubes were synthesized using a facile one-step solution-phase approach with the assistance of nonionic surfactant Polyoxyethylene(20)sorbitan monolaurate (Tween-20), which turned out to be significant for the formation of ultra-long Se submicrotubes. XRD, Raman, SEM, and TEM were adopted to characterize the morphology, structure and phase composition of the as-prepared Se products. It was found that the length of the obtained Se submicrotubes was over 100 pm. By variation of the experimental parameters, the t-Se spheres, nanowires, and broken microtubes can be prepared. The possible growth mechanism of the ultra-long selenium submicrotubes was explained. In addition, we have also demonstrated that the synthesized Ultra-long t-Se submicrotubes using the Tween-20-assisted approach can electrochemically charge and discharge with the high capacity of 265 mAh/g (corresponding to 0.97 wt % hydrogen in SWNTs) under normal atmosphere at room temperature. Cyclic voltammetry was adopted to investigate the adsorption-ox idation behavior of ultra-long selenium submicrotubes. It was observed that the morphology of the synthesized selenium products had a remarkable influence on their capacity of electrochemical hydrogen storage. These differences in hydrogen storage capacity are likely due to the size and density of tubes as well as the microcosmic morphology of different Se samples. The as-obtained ultralong Se submicrotubes are expected to find wide applications in hydrogen storage, high-energy batteries, and optoelectronic, biologic, and catalytic fields as well as in the studies of structure-property relationships. This simple Tween-assisted approach might be extended to the preparations of one-dimensional nanostructures of tellurium and other anisotropic materials.

Study on the Effect of Surfactants on Morphologies of Trigonal Selenium in Microfluidic Reactor

Microfluidic System for Synthesis of Trigonal Selenium Nanowires

Controllable Growth of Se Nanotubes and Nanowires from Different Solvent During the Sonochemical Process

Solution-phase synthesis and electrochemical hydrogen storage of ultra-long single-crystal selenium submicrotubes.

Selective Synthesis Of Single-Crystalline Selenium Nanobelts And Nanowires In Micellar Solutions Of Nonionic Surfactants

Deterministic Growth Of Nanostructures And Microcrystals Of Trigonal Selenium Via Vapor Phase Deposition Routes

The Effects of Different Surfactants on the Morphologies and Electrochemical Properties of MoS2/reduce Graphene Oxide Composites

Effect of Key Parameters on the Morphology Transformation of Three-Dimensional TiO2 Solid Microspheres

Solvothermal syntheses of β-Ag2Se crystals with novel morphologies

Crystallization and Shape Evolution of Single Crystalline Selenium Nanorods at Liquid-Liquid Interface: from Monodisperse Amorphous Se Nanospheres Toward Se Nanorods

Morphology Control of CdSe Nanoparticles Via Two-Step Segmented Microreactors

Preparation of Monodisperse Se Colloid Spheres and Se Nanowires Using Na 2 SeSO 3 As Precursor

Selenium Nanotubes Synthesized by A Novel Solution Phase Approach

Study of the Dissolution Behavior of Selenium and Tellurium in Different Solvents—a Novel Route to Se, Te Tubular Bulk Single Crystals

Synthesis and characterization of Ag2S nanocrystals with different morphologies in micromicelles

Growth of single crystal selenium with different morphologies via a solvothermal method

Effect of ultrasonic-induced selenium crystallization behavior during selenium reduction

Sonochemical Synthesis and Mechanistic Study of Copper Selenides Cu2-Xse, Beta-Cuse, and Cu3se2

A Study of Different Selenium Sources in the Synthesis Processes of Chalcopyrite Semiconductors

Microwave-Assisted Synthesis Of Sb2se3 Submicron Tetragonal Tubular And Spherical Crystals

Surfactant-Controlled Growth of Selenium Nanowires at Room Temperature