Abstract:The nanoparticle-polymer composite is a widely used electronic packaging material. To satisfy the miscibility of nanoparticles with polymer, the surface of nanoparticles needs to be modified. The particle surface modification has been widely studied. However, the interaction between the silane coupling agent (SCA) and the nanoparticle surface is not clear yet. This article aims to investigate the surface modification impact on the nano-SiO 2 particle surface and to clarify the interaction between chemical reagent and the particle surface. In this investigation nano-SiO 2 was characterized by thermal gravity analysis (TGA), Fourier transform infrared spectroscopy (FT - IR), and nano- IR. The FT - IR results showed that the specific peak of SCA appears in the synthesized nano-silica. The TGA experiments were carried out to test the weight loss of SCA modified nano-SiO 2 as well as the grafting efficiency of the surface modification. The FT-IR and TGA results confirmed the SCA chemical grafting onto the nanoparticle surfaces. The nano-IR test provided detailed information for nano-silica surface. It could not only show the topographical AFM images but also the corresponding nanoscale IR adsorption spectra of the nano-silica surface. The topographic image distinguished the nanoparticle from the substrate. The discrete domains spectra shows the existence of SCA on the silica surface, which indicated that the SCA was grafted onto the silica surface with chemical bonding.

Study of Nano-scale Silica Modification by KH-550

Surface Modification of Silica and Its Dispersion in the Hydrogen Silicone Oil

Preparation and surface modification of nano-silica

Effect of Silane Coupling Agent on the Microstructure and Properties of Nanosilica/Resin Composites

Behavior of epoxy resin filled with nano-SiO<sub>2</sub> treated with a Eugenol epoxy silane

Organize modification of silica sol and its application in adhesives

Study of Chemical Modification Onto the Surface of Nano-Sio2

Surface Modification of Nano-Sized SiO2 with Silane Coupling Agent and Its Dispersion

Research of surface modification of nano-SiO2

Coupling of synthesis and modification to produce hydrophobic or functionalized nano-silica particles

Effects Of Silane Coupling Agents On The Electrical Properties Of Silica/Epoxy Nanocomposites

Modification Of Nano-Fibriform Silica By Dimethyldichlorosilane

Surface Modification of Nano γ-Ferric Oxide with Silane Coupling Agent KH-550

Study on Modification and Dispersion of Nano‐silica

Study on preparation and surface modification of precipitated silica obtained from fly ash

MECHANO-CHEMICAL SURFACE MODIFICATION OF NANO SILICA

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

Influences of Surface Modification of Nano-Silica by Silane Coupling Agents on the Thermal and Frictional Properties of Cyanate Ester Resin

Interaction of silane coupling agents with nano-silica probed by nano-IR*

Preparation and Application of Polyurethane Polymer Modified by Nano Silica

Modification of Nanosilica Particles with Hydrophobic Modifier Bis[3-(Triethoxysilyl)propyl]tetrasulfide by Using Micro-Injection in Aqueous Solutions