Abstract:A novel technology, i.e., reactive extrusion, was used to synthesize intumescent flame retardants (IFRs) and their master batches by reacting melamine phosphate (NIP) and pentaerythritol (PER). Limiting oxygen index (LOI), UL94 test, melt flow index (MFI), thermogravimetric analysis (TGA), Fourier transfer infrared (FT-IR) and scanning electron microscopy (SEM) were used to investigate the effect of carbon source (char former/blowing agent ratio) of IFR on the flame retardancy and the water resistance of IFR/Polypropylene (PP) blend. The experimental results show that the char former/blowing agent ratio has a great effect on the flame retardancy and the water resistance of the composite. The flame retardant system, optimally at MP/PER = 1.6 (molar ratio) or additional carbonization agent content = 17.0 wt.% in intumescent system, shows excellent flame retardancy, i.e. UL94 V-0 ratings at both 3.2 and 1.6 mm thickness at 25 wt.% flame retardant (FR) loading, and UL94 V-0 rating at 3.2 mm thickness at 20 wt.% FR loading in IFR/PP formulation. Also, the water resistance of flame-retarded material was improved greatly by selecting a reasonable char former/blowing agent ratio, i.e. at MP/PER = 1.6 (molar ratio) or additional carbonization agent content = 17.0 wt.% in intumescent system, IFR/PP blend at 25 wt.% flame retardant loading can still reach UL94 V-0 rating after treatment with water at 70 degreesC for 168 h. The polarity of IFRs, dispersion of IFRs in PP matrix and compatibility of IFRs with PP matrix were also found to influence the water resistance of 1FR/PP blend based on IR, water solubility test and SEM. The thermal stability of IFR/PP blend, affected by char former/blowing agent ratio, was proved to be well correlated with its flame retardancy whether before or after water treatment. (C) 2003 Elsevier Science Ltd. All rights reserved.

An Efficiently Halogen-Free Flame-Retardant Long-Glass-Fiber-Reinforced Polypropylene System

Flame Retardation and Thermal Degradation of Intumescent Flame‐retarded Polypropylene Composites Containing Spirophosphoryldicyandiamide and Ammonium Polyphosphate

Preparation and Flame Retardancy of Intumescent Flame-Retardant Polypropylene

Flame Retardant Synergy Between Interfacial and Bulk Carbonation in Glass Fiber Reinforced Polypropylene

A Intumescent Flame-Retardant Polypropylene System and Its Burning Behaviors

Performance of Intumescent Flame Retardant Master Batch Synthesized Through Twin-Screw Reactively Extruding Technology: Effect of Component Ratio

Thermal Degradation and Combustion Behavior of Novel Intumescent Flame Retardant Polypropylene with N-alkoxy Hindered Amine

Synergistic effects of 4A zeolite on the flame retardant properties and thermal stability of a novel halogen-free PP/IFR composite

The Multilayered Distribution of Intumescent Flame Retardants and Its Influence on the Fire and Mechanical Properties of Polypropylene

Synergistic effects of ferric pyrophosphate (FePP) in intumescent flame-retardant polypropylene

Flammability and Thermal Properties of a Novel Intumescent Flame Retardant Polypropylene

Organically Modified Montmorillonite As A Synergist for Intumescent Flame Retardant Against the Flammable Polypropylene

Mechanical, Dielectric and Flame-Retardant Properties of GF/PP Modified with Different Flame Retardants

Synthesis of a Novel Intumescent Flame Retardant and Its Flame Retardancy in Polypropylene

Flame Retardant Mechanism of a Novel Intumescent Flame Retardant Polypropylene

Mechanical, Flame-Retardant and Dielectric Properties of Intumescent Flame Retardant/Glass Fiber-Reinforced Polypropylene through a Novel Dispersed Distribution Mode

Synergistic Effect of Compound Oxides with Intumescent Flame Retardant on the Properties of Polypropylene Composites

An Investigation on the Flammability of Halogen-Free Fire Retardant PP–APP–EG Systems

Synergistic effect between a char forming agent (CFA) and microencapsulated ammonium polyphosphate on the thermal and flame retardant properties of polypropylene

A Novel Intumescent Flame‐retardant LDPE System and Its Thermo‐oxidative Degradation and Flame‐retardant Mechanisms

Effect of modified layered double hydroxide on the flammability of intumescent flame retardant PP nanocomposites