Abstract:The cerium ion (Ce4+) modified titania sol and nanocrystallites were prepared by chemical coprecipitation–peptization and hydrothermal synthesis methods, respectively. XRD patterns show that Ce4+-TiO2 sol particles had anatase semicrystalline structure. And the calcined Ce4+-TiO2 powder was composed of predominant anatase titania and crystalline cerium titanate (11.18wt.% CexTi(1−x)O2). AFM micrograph shows that ultrafine particles were well dispersed in sol system and average particle size was about 10nm. Ce4+-TiO2 nanocrystallites have grown into 70nm in mean size. The difference in calculated particle size (2.41nm for sol particle and 4.53nm for crystallite) by XRD Scherrer’s formula was mainly due to aggregation effect of nanoparticles. The experimental results exhibit that Ce4+-TiO2 sol and nanocrystallites can effectively photodegrade reactive brilliant red dye (X-3B) with the dye/Ce4+-TiO2/visible-light reaction system. Moreover, photocatalytic reaction also can carry out in hydrosol reaction system as well as in suspension reaction system. And Ce4+-TiO2 sol has shown higher efficiency than nanocrystallites in respect of photocatalytic activity. Meanwhile, dye photodegradation mechanisms involving photolysis, photocatalysis, photosensitized photocatalysis and interband photocatalysis were proposed regarding different photocatalytic reaction system.

Preparation of Supported TiO2 and Degradation of Active Brilliant Red X-3B

Study on Preparation and Photocatalytic Properties of TiO_2/SiO_2 Composite Powders

Preparation of TiO_2/SiO_2 and Photo-Catalytic Degradation of Methyl-Orange

Preparation of Supported TiO2 and Its Behaviors for Degradation of Alizarin Red

Preparation and Characterization of Nano TiO2/SiO2 Catalyst

Preparation of TiO2/SiO2 and kinetics for degradation of alizarin red over TiO2/SiO2

The Preparation of Nano-Tio2 Material under the Control of Organic Substance and Study on Its Photo Catalytic Activity

Study on Preparations and Characters of TiO2 Photocatalysts Supported on Porous Materials

Photocatalytic degradation of textile dye X-3B using TiW11Ti/SiO2 hybrid materials

Studies on Preparation and Characterization of 3DOM TiO2 and TiO2/SiO2 Materials with High Photocatalytic Ability

Study on Photocatalytic Degradation Kinetics of Reactive Brilliant X-3B in Different Irradiance

PHOTOCATALYTIC DECOLORIZATION OF ACTIVE RED X-3B BY ULTRAFINE TiO2 PARTICLES SYNTHESIZED IN HIGH TEMPERATURE AEROSOL REACTOR

Preparation and Photocatalytic Performance of Fixed Titanium Dioxide Film

Sol-Gel Preparation and Characterization of High Activity Titanium Dioxide Nanocrystalline Photocatalyst

Preparation of La3+-TiO2/Clinoptilolite Photocatalyst and Its Photocatalytic Activity for Methyl Orange

Preparation and Characterization of Nanosized TiO2 Films as Photocatalysts

Visible-light responsive cerium ion modified titania sol and nanocrystallites for X-3B dye photodegradation

Study on the Photocatalysis Performance and Degradation Kinetics of X-3B over Modified Titanium Dioxide

Photocatalytic Degradation of the Reactive Brilliant Red and Its Mechanism over Nano-sized TiO2-Cu2O Under Visible Irradiation

Study on preparation of TiO_2 loaded on activated carbon and photocatalytic properties

Preparation of Ti-heteropolyacid/TiO 2 and its rapid photocatalytic degradation of X-3B