Preparation, Water-Redispersibility and Water Resistance of Self-Crosslinking Redispersible Styrene-Acrylate Copolymer Powder
ZHU Zu-wei,ZHOU Li-zhuang,SITU Yue,HUANG Hong,LAN Ren-hua,CHEN Huan-qin
DOI: https://doi.org/10.3969/j.issn.1003-9015.2013.03.023
2013-01-01
Abstract:Self-crosslinking redispersible styrene-acrylate copolymer powder with both excellent water-dispersibility and good water-resistance was prepared via spray drying by adding self-crosslinking monomer,N-Methylolacrylamide(NMA),to the shell of the latex particles.FT-IR,TEM,SEM,Malvern particle size analysis and AFM were adopted to characterize the original emulsion,polymer powder or redispersion emulsion.The neutralization,spray drying and redispersion process of the emulsion were studied respectively and the mechanism of the emulsion having both the properties of water-redispersibility and water resistance was investigated.The self-crosslinking styrene-acrylate emulsion possesses uniform nano-scale soft core/ hard shell structure.The particle sizes of redispersible polymer powders are in the range of 2~20 μm,whereas the average latex particle size of dispersion emulsion is 182 nm,which indicates that the polymer powder possesses excellent water-redispersibility.Thicker "hairy structure" and hydrated shell are formed in the neutralization process because the hydrophobic interaction is weekend by adding NMA monomer into the shell of styrene-acrylate latex particles.During the transient drying process,fusion and crosslinking between different latex particles are impeded because of longer physical distance,and therefore better redispersibility is obtained.The water absorption of polymer film made from self-crosslinking redispersible polymer powder is lower than that of unmodified polymer powder by 40%.Hence both water-redispersibility and water resistance of styrene-acrylate copolymer powder can be improved by the self-crosslinking modification of NMA.