Sulfonated polystyrene and its characterization as a material of electrolyte polymer
Ngadiwiyana,Ismiyarto,Gunawan,RS Purbowatiningrum,N.B.A. Prasetya,T.D. Kusworo,H. Susanto
DOI: https://doi.org/10.1088/1742-6596/1025/1/012133
2018-05-01
Journal of Physics: Conference Series
Abstract:The research of polystyrene modification from Styrofoam waste and its application as a main material of electrolyte polymer had been done. The sulfonation reaction of polystyrene was conducted using sulfuric acid as sufonation agent and the reactions were done with variation times of 1, 2, 3, 4 and 5 h. The characterization of the sulfonated products covered analysis of functional groups using FT-IR spectrophotometer, sulfonation degree, measurements of ion exchange capacity, conductivity and swelling degree. The sulfonated polystyrene product was white solid as confirmed by the spectra of FT-IR with the presence of wide band absorption of O=S=O at the wavenumber of 1080-1411 cm-1 as indication. The research showed the best sulfonated polystyrene prepared in 4 h as a material of electrolyte polymer, since it had the highest degree of sulfonation, ion exchange capacity, conductivity and swelling degree with the values were 28.52 %, 1.550 meg/g, 15,924.10-6 Ω-1cm-1 and 332.4 %, respectively.