Microstructure and Mechanical Properties of Free-cutting 2011 Aluminum Alloy

HUANG Zhi-qi,YIN Zhi-min,FENG Ze-xi,CAI Man-hai,ZENG Qi-cai

DOI: https://doi.org/10.3969/j.issn.1005-4898.2006.02.007

2006-01-01

Abstract:The effect of aging treatment on the microstructure and mechanical properties of solution treated and cold drawn 2011 alloy was investigated by mechanical performance test,XRD analysis,DTA thermal analysis and TEM observation.The results show that the best aging process is 170℃/8h,in which the tensile strength, yield strength and the elongation of the alloy bar can reach 472MPa,378MPa and 10.1%respectively.The phase compositions include Al-based solid solution,low melting point eutectic(Pb_7Bi_3+Bi)and θ′CuAl_2 precipitates.The melting point of spherical eutectic(Pb_7Bi_3+Bi) is 156.02℃.The existence of low melting point eutectic(Pb_7Bi_3+Bi) and the precipitation strengthening of θ′CuAl_2 phase give the alloy not only good strength but also excellent machining properties.