Highly Dispersing Melamine Cyanurate Flame Retardant Nylon 66

Liu Pengju,Liu Yuan,Wang Qi,Song Lei

DOI: https://doi.org/10.3969/j.issn.1001-3539.2013.03.002

2013-01-01

Abstract:According to the disadvantages of existing commercialization melamine cyanurate(MCA) such as MCA having rigid agglomerate particle structure and high hardness,as well as its difficult dispersion in nylon 66(PA66) matrix leading to deterioration of flame retardance and mechanical properties of MCA flame retardant PA66,a highly dispersing MCA(FS–MCA) synthesized by self was employed to flame-retard PA66.Particle morphology,dispersion behaviors and the corresponding mechanism of FS– MCA were investigated by waterborne dispersion experiment and SEM.Vertical flame test,micro-scale combustion calorimetry,tensile and impact strength tests were used to study combustion behaviors,flame retardance and mechanical properties of MCA and FS–MCA flame retardant PA66.The results show that FS–MCA has weaker inter-particle combination and looser agglomerate particle structure compared with MCA,thus leads to its ultrafine(submicron scale) dispersion in PA66 resin matrix.When the mass fraction of FS–MCA is 10%,FS–MCA flame retardant PA66 can achieve UL 94 V–0 rating(1.6 mm) and its tensile strength,elongation at break,notched impact strength are 80.6 MPa,11.4%,7.9 kJ/m2 respectively,these are better than that of existing commercialization MCA flame retardant PA66 system.