Abstract:A first principles calculation is used to simulate the variation of the lattice constant, structure, induced charge-density difference, total energy, and band gap of the hexagonal and cubic MgZnO semiconductor alloys with different MgO mole fractions. The calculated results show that the lattice constant and the ratio c/a of the hexagonal MgxZn1-xO diminish as the MgO mole fraction is increased, which results in the structure gradually deviating from the wurtzite structure. The angle between the nearest neighbor Zn-O bonds is larger than that between the nearest neighbor Mg-O bonds. The total energy of the hexagonal alloys is lower than, equal to, and larger than that of the cubic one in the lower MgO mole fraction, the MgO mole fraction with 0.69, and the higher MgO mole fraction, respectively. The phase transition is likely to occur as the MgO mole fraction is increased. The crystal structure will become unstable as temperature is raised to a critical value for the different MgO mole fractions no matter what kind the structure is. The band gaps of the hexagonal and cubic MgxZn1-xO alloys are the direct type and widen as the MgO mole fraction is increased, which demonstrates that both the structures of the MgxZn1-xO alloys are suitable for fabricating the short wavelength devices.

The Structural Properties of Wurtzite and Rocksalt MgxZn1−xO