Effects of acetic acid/acetic anhydride ratios on the properties of corn starch acetates
Cherif Ibrahima Khalil Diop,Hai Long Li,Bi Jun Xie,John Shi
DOI: https://doi.org/10.1016/j.foodchem.2010.12.050
IF: 8.8
2011-01-01
Food Chemistry
Abstract:Corn starch was pre-treated with acetic acid and then acetylated by acetic anhydride under microwave irradiation. The effects of molar ratios of these two reagents on the acetylation of starch were investigated. Starch acetate with a high degree of substitution (DS, 2.93) was obtained at a molar ratio (acetic acid/acetic anhydride) of 1:1. However, the DS should tend to decrease with a change of this ratio. The FT-IR analysis indicated characteristic absorption peaks, with increasing DS materialised by an increase of the carbonyl C O group and a decrease of the hydroxyl O–H group, at about 1750 cm −1 and 3450 cm −1 , respectively. The X-ray diffraction patterns of acetylated starch showed an amorphous structure. Degree of crystallinity, surface morphology, water solubility and water absorption index of corn starch were also affected by the changes in reagent ratios. The glass transition ( T g ) and melting ( T m ) temperatures of acetylated starches also decreased after acetylation. Keywords Acetic acid/acetic anhydride ratios Corn starch Acetylation Degree of substitution Microwave heating Physical properties 1 Introduction In recent years, interest in finding environmentally friendly alternatives to nondegradable plastic materials made from petroleum has placed an emphasis on natural molecular materials from agricultural sources ( Xu, Miladinov, & Hanna, 2004 ). Starch is one of the most widely used natural biopolymers because of its low cost, abundant availability and renewability and has been one of the best choices for the aforementioned uses. Unfortunately, due to its hydrophilicity, its poor mechanical properties and its dimensional stability, especially in the presence of water and in humid environments ( Wang et al., 2008 ), untreated starch is somewhat unsuitable for non-food use. To overcome these shortcomings, over the past 15 years, many papers have been published describing the modification of starch to turn it into a thermoplastic material. Chemical modifications are necessary to significantly improve the mechanical properties of natural polymers. Esterification of starch leads to a product with a good thermoplastic processability enhanced mechanical properties and an increased hydrophobicity. Depending on the degree of substitution (DS), some of the highly hydrophilic hydroxyl groups in the anhydroglucose units of starch are converted to more hydrophobic acetyl groups. Acetylation is one such method that has received significant attention in recent years. Acetylation can be performed with relative ease to significantly improve the physicochemical and functional properties of the starch, even at low DS ( Xu et al., 2004 ). Indeed, acetylated starches with a relatively low degree of substitution (DS) have been widely used in the food industries for many years ( Saartrat, Puttanlek, Rungsardthong, & Uttapap, 2005 ). However, high DS (DS from 2 to 3) acetylated starches were of research interest from 1950 until recently because of their solubility in solvents such as acetone or chloroform and for their thermoplasticity ( Elomaa et al., 2004 ). These polymers have been used for non-food applications, such as tablet binders, hot melt adhesives, coatings, cigarette filters, biodegradable plastic and metal ion absorbents ( Biswas et al., 2008 ). On the other hand, starch acetates with high DS have been prepared with the aim to replace cellulose acetate. Acetic anhydride is commonly used as a versatile acetylating agent of organic substrates, essentially involving the substitution of free hydroxyl groups. During acetylation, three free hydroxyl groups on C2, C3 and C6 of the anhydroglucose unit of the starch molecule can be replaced with acetyl groups in a kinetically controlled reaction; therefore, the theoretic maximum DS is three. In fact, these three free –O–H groups have different reactivities. The primary –OH on C6 is more reactive and is acetylated more readily than the secondary ones on C2 and C3 due to steric hindrance ( Xu et al., 2004 ). Between the other two –OH groups, the OH on C2 is more reactive than is the one on C3, mainly because the former is close to the hemi-acetal and more acidic than the latter. Starch granules form a succession of crystalline and amorphous lamellae made of a highly branched amylopectin double helical chain and an amylose linear chain, respectively. Pretreatment with hot water or in an organic solvent (DMSO, carboxylic acid), in order to activate the starch molecule, might be necessary in some cases to influence the reaction rate, with or without the use of catalysts. Frequently, bases such as pyridine and concentrated sodium hydroxide are used as catalysts. Recently, for special reactions, certain salts or iodine, acting as a Lewis acid, are also in use. Theoretically, all reactions require energy input ( Li et al., 2009 ). The use of microwave energy in organic synthesis is becoming very popular and many reactions are becoming accessible with amazing results. The main advantage of using microwaves to assist reactions is that the reaction can be achieved under solvent-free conditions (eco-friendly process or green chemistry compared to conventional heating), thus leading to a reduction in the amount of waste produced and of the reaction time, even by an order of magnitude. When microwave energy is applied to a material having permanent electric dipoles and monopoles (ionic charges), a portion of the incident energy is reflected from it and the remaining energy is transmitted into the material. By random collisions with neighbouring molecules, the dipoles transfer energy, resulting in a temperature rise in the material. When acetic acid is heated with microwaves, its temperature rises to about 1.5 times that of water for the same energy input, and this temperature rise (twice that for water) occurs in the case of acetic anhydride ( Brelid & Simonson, 1999 ). Furthermore, the great ability of iodine to absorb microwaves improves the reaction and shortens the time, thus avoiding loss in molecular weight of the final product ( Feuer & Heights, 1998 ). The objectives of our study were to determine the influence of the molar ratios of acetic acid and acetic anhydride on the acetylation of corn starch when assisted by microwaves and catalysed by iodine and to evaluate the properties of the resulting products. 2 Materials and methods 2.1 Materials Native corn starch (molecular weight (Mw) = 115.8 ± 1.12 × 10 6 g/mol, 25% amylose content) was dried at 50 °C for 24 h before processing (moisture content about 3.22%). Acetic acid and acetic anhydride were of analytical grade 99% (Shanghai Chemical Reagent Co. Ltd.) sodium thiosulfate (Jiaozuo Chemical Factory, Jiaozuo, PR China), ethanol (Sinopharma Chemical Reagent Co. Ltd., Shanghai, China), 98% sulphuric acid (Xin Yang chemical reagent Company, Henan, PR China) and analytical grade iodine (The Chemical Factory of Hubei University, Wuhan, China) were used as received. 2.2 Analytical equipment Equipment consisted of: a Microwave Apex Atmospheric Pressure, Microwave Synthesis/Extraction System (Shanghai EU Microwave Chemistry Technology Co. Ltd.), FT-IR (Thermo Nicolet NEXUS 670 FTIR), DSC (NETZSCH 204F1, Germany), SEM (JEOL, JSM-6390/LV, Japan) and X-ray diffractometer (Bruker AXS/D8 Advance, USA). 2.3 Methods 2.3.1 Synthesis of starch acetate A sample of 4.86 g (30 mmole; 3.22% moisture content) of native corn starch was put into a 50 ml three-neck round-bottom glass flask with a mechanical stirrer and a reflux condenser, followed by mixtures with different molar ratios of acetic acid:acetic anhydride with a total amount of these reagents fixed to 180 mmole. 1.75 mmole (0.222 g) of iodine was used as catalyst for each starch:acetic acid:acetic anhydride ratio. Acetic acid (0, 30, 60, 90 and 120 mmole) was added to the starch and stirred at room temperature for 10 min. According to the volume of acetic acid used, acetic anhydride (180, 150, 120, 90 and 60 mmole), was added dropwise and the mixture stirred for 5 min before the addition of iodine. When the solution was uniformly mixed, the three-neck flask was placed in the microwave oven, equipped with a reflux condenser and a fibre optic temperature probe. The acetylation was performed at 100 °C under stirring, for a constant period of 2 min under an irradiation power of 300 W. At the end of the reaction, the flask was removed from the microwave oven, and cooled to room temperature. A saturated solution of sodium thiosulfate (2 ml) was added to the mixture, and stirred until the mixture colour changed from dark brown to colourless, indicating the transformation of iodine to iodide. Then the mixture was precipitated with ethanol, filtered, washed with ethanol and distilled water to remove the unreacted acetic acid and byproducts and then dried at 50 °C overnight. The acetylated starches obtained from these different conditions were first ground to a fine powder before further analysis. 2.3.2 Determination of the degree of substitution (DS) Determination of the DS by titration involved complete basic hydrolysis of the ester linkages and titration of the excess alkali, following the method used by Nutan (2004) with a slight modification. A sample of 0.50 g of native (blank) and ground starch acetate, accurately weighed, was added to 25 ml of 75% (v/v) ethanol solution. The slurry was stirred in a water bath at 50 °C for 30 min. After the slurry was cooled to room temperature, 20 ml of a solution of 0.5 N KOH was added to the slurry and the solution was occasionally shaken for 72 h to complete saponification at room temperature. The excess of alkali in the solution that leached from the sample was titrated with 0.5 N HCl, using the phenolphthalein as an indicator. Acetyl content (%A) was calculated according to the following equations (1) % A = [ ( V 0 - V n ) × N × 43 × 10 - 3 × 100 ] / M where V 0 = volume (ml) of HCl used to titrate blank, V n = volume (ml) of HCl used to titrate sample, N = normality of used HCl, M = sample amount as dry substance (g), 43 = weight of acetyl group. Acetyl content (%A) was used to calculate the degree of substitution, DS, following equation (2) : (2) DS = 162 × % A / [ 43 × 100 - ( 43 - 1 × % A ) ] where 162 = molecular weight of the anhydroglucose unit, 1 = the hydrogen mass. 2.3.3 Fourier transform-infra red (FT-IR) analysis Fourier transform-infrared (FT-IR) spectra of the native and acetylated starches were obtained for the dried powder at a wave number range of 4.00–400 cm −1 . Pellets were prepared from mixtures of the samples and KBr (1:50 by weight). Thirty-two scans were accumulated at a resolution of 4 cm −1 . 2.3.4 X-ray diffraction analysis The X-ray diffraction pattern was obtained from a conventional copper target X-ray tube set to 40 kV and 40 mA. The X-ray source was Cu Kα radiation. Data were collected from 2 θ of 5.00–35.00° ( θ being the angle of diffraction), with a step width of 0.02°, a step time of 0.4 s, a scanning speed of 15°/min, a divergence slit width of 1 mm, a scatter slit width of 1 mm, and a receiving slit width of 0.3 mm at room temperature. Native and acetylated starch samples were dried at 50 °C to a constant moisture content (3%) in a vacuum oven; then samples were added into the slide for packing prior to X-ray scanning ( Chi et al., 2008 ). MDI Jade 5 software was used for the analysis of the spectra and the determination of the degree of crystallinity. 2.3.5 Differential scanning calorimetry (DSC) analysis DSC measurements were performed with a NETZSCH 204F1 DSC. About 7 mg of the dried samples (0.03% moisture content) were placed in aluminium DSC pans, and the pans were sealed. The instrument was calibrated with indium. Samples were heated from 30 to 300 °C with a heating rate of 10 °C/min in a nitrogen atmosphere. The glass transition temperature ( T g ) and melting temperature ( T m ) were taken as the inflection point of the increment of special heat capacity and as the peak value of the endothermic process in the DSC curves, respectively ( Xu, Dzenis, & Hanna, 2005 ). 2.3.6 Scanning electron microscopy (SEM) analysis The morphological features of the native starch and starch acetates with different DS were observed with a scanning electron microscope. The dried samples were mounted on a metal stub and sputtered with gold in order to make the sample conductive, and the images were taken at an accelerating voltage of 10 kV. Micrographs were recorded at 10,000× magnification to assure clear images ( Zhang, Xie, Zhao, Liu, & Gao, 2009 ). 2.3.7 Water absorbance index (WAI) and water solubility index (WSI) WAI and WSI of native and modified corn starch were measured by a procedure similar to AACC method 56-20 (1983). To determine WAI and WSI, the starch samples were ground to pass through an 80 mesh sieve. The samples (about 1 g) were dispersed in 30 ml of distilled water in pre-weighed centrifuge tubes. The centrifuge tubes were placed in a shaking water bath at 30 °C for 30 min, and then centrifuged at 4000 g for 15 min. The supernatants were decanted carefully into pre-weighed glass dishes, dried at 105 °C for 12 h, cooled to room temperature and weighed. The remaining sediment in the tube was weighed. WAI (g/g) and WSI (%) were calculated ( Xu et al., 2005 ): (3) WAI = [ W s - W t / W 1 ] where W s = weight of tube with the sediment, W t = weight of the empty tube, W 1 = weight of the dry sample and (4) WSI = [ W 3 - W 2 / W 1 ] × 100 where W 3 = weight of the dish and with dry solute, W 2 = weight of the empty dish, W 1 = weight of the dry sample. 2.3.8 Statistical analysis The different effects of the reagent ratios on the reaction were analysed with SPSS 16.0 and origin pro.8 software. Analysis of variance (ANOVA) was performed and the significance estimated ( p < 0.05). 3 Results and discussion 3.1 Degree of substitution (DS) Starch acetates with high DS were synthesised by the reaction of starch with anhydride using iodine as a catalyst and under the assistance of microwaves. The iodine content, the reaction temperature and the reaction time were deliberately fixed during the reaction, to limit the study of the effects of the ratio between acetic acid and acetic anhydride (mole/mole) on the variation in the DS. The DS of acetylated starches determined by the saponification titration method are summarised in Table 1 . The highest DS was 2.93. This DS is relatively high, three being the theoretical maximum DS ( Nutan, 2004 ). 3.2 Effect of acetic acid:acetic anhydride molar ratios on esterification The impact of the reaction agent (acetic acid/acetic anhydride) molar ratios on the DS was evident during the acetylation ( Fig. 1 B). From an acetic acid/acetic anhydride ratio of 2:1–1:1 (mole/mole), an increase of the DS is noted; however, the DS rapidly decreases with a decrease of this molar ratio (1:1–0:1). In this reaction, the pretreatment with acetic acid could activate the reactive portions of the starch molecule, which accelerated the esterification with acetic anhydride, and effectively enhanced the DS. Nevertheless, the major role, in the esterification, is played by the acetic anhydride. Shogren (2008) indicated that the gelatinisation of starch in acetic acid prior to reaction could accelerate the acetylation with acetic anhydride. A large amount of acetic anhydride is usually required to stimulate its collision with the reactions sites in the starch molecule ( Xu et al., 2004 ). However, the evolution of the DS observed indicates the necessity to consider a relative equilibrium between acetic acid and acetic anhydride in the reaction environment in order to get a better yield. Indeed, the ratio 1:1 of these two reagents gave the best condition to obtain the highest DS. Iodine, acting as a Lewis acid catalyst ( Fig. 1 A), is able to accept two pairs of electrons from other reactants in the reaction medium; this could activate the carbonyl carbon of acetic anhydride, making the latter more reactive ( Li et al., 2009 ). As a control, starch was acetylated without the intervention of iodine as catalyst, by using a reagent molar ratio of 1:1 under the same conditions of time and temperature. A low DS of about 0.25 was obtained ( Table 1 ). 3.3 Fourier transform-infra red (FT-IR) analysis The FT-IR spectra of native and acetylated corn starches are shown in Fig 2 . In the IR spectrum of native starch, there are several discernible peaks at 1018 cm −1 , 1080 cm −1 , and 1157 cm −1 , which were attributed to the C–O bond stretching. Other characteristic absorption bonds were observed at around 1641 cm −1 , corresponding to the tightly bound water (H 2 O) in the starch, an extremely broad band at around 3450 cm −1 , resulting from the vibration of the hydroxyl group (O–H) and at around 2960 cm −1 , attributed to the C–H vibration stretch. After acetylation by acetic anhydride, new absorption bands appeared at 1750 cm −1 , 1435 cm −1 , 1373 cm −1 and 1240 cm −1 , assigned to the carbonyl C O, to the CH 3 antisymmetry deformation vibration, to the CH 3 symmetry deformation vibration and to the carbonyl C–O stretch vibration, respectively. These new absorption bands suggest that the ester carbonyl groups were formed during the esterification process in starch, namely, the acetylated starch products synthesised ( Chi et al., 2008 ). The intensity, the area, and the height of these peaks are highly dependent on the degree of substitution. With increasing DS, the intensities of the peaks, area and height, at approximately 3450 cm −1 , 1080 cm −1 , 1018 cm −1 , particularly those related to the O–H vibration, were gradually weakened and they almost disappeared when the DS reached 2.93, indicating that the hydroxyl groups have perfectly participated in the reaction. By contrast, the parameters cited above, involving peaks associated with the carbonyl ester (C O) at 1750 cm −1 and 1435 cm −1 , and peaks related to the methyl of the acetyl group, at 1240 cm −1 and 1373 cm −1 , showed a significant increase with increasing DS ( Biswas et al., 2007 ). From Figs. 2 and 3 we observed that the ratio between peak area and peak height attributed to the O–H group at 3450 cm −1 (OH peak) exhibited a negative correlation with the DS ( R 2 = 0.9815, p = 0.000), and a positive correlation between the same ratio and the DS for the peak attributed to the C O group at 1750 cm −1 (CO peak) ( R 2 = 0.911, p = 0.003) was noticed. These values demonstrated that the depression of the O–H peak and the observed rise in the C O peak could explain the relationship between the proportion of C O and O–H groups in the starch molecule and the increase of the degree of substitution. The absence of the peak in the region 1850–1760 cm −1 implied that the product was free of unreacted acetic anhydride, and the absence of absorption in the area of 1700 cm −1 for the carboxylic group indicated that the product was also free of acetic acid byproduct; the same observation was reported by Li et al. (2009) . 3.4 X-ray diffraction The necessity to perform the X-ray diffraction (XRD) measurement is explained by the fact that acetylation can alter the crystallinity of corn starch ( Chi et al., 2007 ). The XRD analysis results for native and acetylated corn starches are shown in Fig. 4 C. The spectrum of the native corn starch showed an A-type crystal pattern, characteristic of cereal starch, with strong reflections at around 2 θ of 15.8° and 23° and an unresolved doublet at around 17.8° and 18.8°. For the modified starches, this structure was totally changed, and new patterns showing wide peaks at 2 θ of 9° and 20° were observed, representing the typical structure of acetylated starch. The relative increase in the intensity of the peak at 20° (2 θ ) could be attributed to the V-type complex. The formation of this structure was presumably mostly the result of the association of starches, especially its amylose chain with the acetyl ester group. An anhydrous V-type structure is usually favoured when a bulky group is grafted onto the starch chain ( Aburto et al., 1999 ), making the starch more hydrophobic. After the esterification, an important loss of the degree of crystallinity was detected as compared with the native starch. The degrees of crystallinity decreased from 20.32% to about 7% with the increase in DS ( Fig. 4 A), which indicated that, with esterification processing, the crystalline structure of the native starch was destroyed. Fig. 4 C shows that the acetic acid has an influence on the crystalline structure of the modified starch. The degree of crystallinity in cereal starch is largely attributed to the formation of double helices by intermolecular hydrogen bonds within the amylopectin segments. In fact, as corroborated by the FT-IR analysis, after esterification, acetyl groups replace some hydroxyl groups on starch, reducing the formation of inter and intramolecular hydrogen bonds, resulting thereby in the destruction of the original ordered crystal structure ( Zhang et al., 2009 ). The use of iodine as catalyst also caused the disintegration of the native structure of starch ( Cheetham & Tao, 1998 ). After the acetylation reaction, the small amount of crystal remaining in the starch could be responsible for the broad peaks recorded ( Xu et al., 2004 ). 3.5 DSC (differential scanning calorimetry) analysis The changes in heat capacity (Δ Cp ), glass transition temperature ( T g ) and melting temperature ( T m ) of native corn starch after the acetylation were determined via DSC ( Table 1 ). All the samples were dried at 105 °C for 2 h before analysis, leading to a moisture content of 0.3%. The thermal (DSC) curve for native starch showed a broad exothermic peak between 50 and 150 °C, but this peak was not observed after the acetylation. This peak could be attributed to the reaction of the binding water with the starch molecule during the heating process. The T g measured at the midpoint of the transition was considered in this study. Chung, Soo, and Lim (2003) and Singh, Kaur, and Mc Carthy (2007) reported that the glass transition of raw granular starch, under limited water conditions, is difficult to measure due to the low heat capacity change at T g , but also due to the thermal degradation of starch polymers at elevated temperature. However, Forsell, Mikkilä, Moates, and Parker (1997) estimated the T g of dry amylopectin and amylose to be approximately 230 °C, and a calculated T g of 243 °C was obtained for corn starch by using the Fox and Flory equation ( Cauvain, 2003; Qiang, Su, & YI, 1999 ) with a Δ Cp of 0.425 J/g °C. From Table 1 , we noticed that the T g of the starch acetate made with a molar ratio of acetic acid:acetic anhydride of 1:1 and DS of 2.93 was 155.3 °C, which is estimated to be about 75–88 °C lower than its unmodified counterpart. This variation can be explained by the rupture of the amylopectin double helices after the substitution of the hydroxyl groups by bulkier acetyl groups ( Singh, Kaur, & McCarthy, 2007 ). The incorporation of the ester group into a starch molecule augments the free volume inside the chain and reduces the tension provoked by the intermolecular hydrogen bond, showing an increase of the molecular mobility in the rubbery state ( Schuck, Mejeans, Dolivet, Jeantet, & Bhandari, 2007 ). As expected, a relative reduction in the T g with an increase in the DS was observed, but this diminution was feeble as noted in Table 1 . Another transition assigned to the melting point ( T m ) of the corn starch appears after the glass transition. For the native starch, this transition is characterised by a broad peak with two distinct phases, typical of the melting of the A-type crystal, that exists in cereal starches ( Qiang et al., 1999 ). This peak was estimated at about 290 °C (Δ Hm ; 2.3 J/g). However, it was noticed that the values of T m for acetylated starch were slightly lower than those for native starch, but acetylated starch exhibited a single transition at the melting point. Considering the various ratios of acetic acid:acetic anhydride, the melting point did not show a wide variation in temperature, which oscillated between 270 and 282 °C, with a huge reduction in the energy (Δ Hm ) observed, compared to the raw sample. Starch acetates with high DS (DS > 2) prepared under these conditions have shown interesting thermoplastic and thermostable properties. 3.6 Scanning electron microscopy (SEM) Fig 1 shows the morphology of native corn starch before and after acetylation with different ratios of acetic acid and acetic anhydride. Native corn starch granules showed irregular polygonal shapes with a smooth surface and a mean diameter of about 10 μm. This morphology has also been remarked upon by Chung and Lai (2006) . Jie, Peng, Sheng, Xing, and Tong (2006) confirmed that microwave irradiations had no significant effects on the morphology of the corn starch granule. However, after esterification, the structures of the granule surface were completely changed in comparison to the unmodified starch. The initial smooth appearance was turned to a rough surface lined with various diameters of holes. As the DS of the starch acetates increased, aggregations and porosity increased on the surface of the acetylated starch granules. These morphological transformations could be attributed to the fusion of granules caused by the disruption of the starch during the heating process. Moreover, we observed that the surface aggregation of granules was correlative with the molar ratio of acetic acid:acetic anhydride. In Fig 5 B and D we note that the granule surfaces of starch acetates with the same DS (2.65) showed different structures, and this observation corroborated the fact that variations of the surface morphology were strongly related to the change in the reagent ratios. Singh, Chawla, and Singh (2004) reported that acetylation brought the granule to fusion due to its reaction with high amounts of acetic anhydride. Indeed, during the reaction, starch granules lost their integrity and were split, melted and re-associated to form new structures ( Yan & Zhengbiao, 2010 ). This fusion was largely the consequence of the introduction of bulky acetyl group, which disrupted the internal structure and weakened the granule, but was also due to the coalescing of starch granules together. Acetylation of starch occurs preferentially in the amorphous region of the granule, which is composed of amylose. Due to the poor penetrability of acetic anhydride into the starch granule, the outer lamella of the crystalline lamellae is predominantly involved ( Chen, Schols, & Voragen, 2004 ). However, during acetylation, the granule became looser and more porous, which accelerated the esterification, making the starch acetate granules turn into small fragments ( Wang et al., 2008 ). Thus SEM results showed that strong erosion occurred on the morphology of native corn starch after esterification. The extent and the characteristics of these alterations were related to the variation of the ratio of acetic acid and acetic anhydride. 3.7 Water absorption index (WAI) and water solubility index (WSI) As demonstrated in Fig. 4 A and B, starch acetates with different degrees of substitution (DS) showed an increase of the index of their absorption and solubility in water at room temperature, in comparison to the native starch. Fig 4 A shows that the water solubility index (WSI) was maximal with a DS of 1.83 and subsequently diminished when the degree of substitution increased. However, a slightly different behaviour was observed concerning the water absorption index (WAI), which was augmented with the increase of the DS, then started to decrease when the DS reached 2.65. According to our results, the degree of acetylation could have an influence on both the water solubility and the water absorption of acetylated starches and a similar observation was pointed out by Shogren and Biswas (2006) and Xu et al. (2005) . The surface erosion ( Fig. 5 ) noticed with the variation of the molar ratio of acetic acid to acetic anhydride in the reaction medium, could indirectly affect the absorption and the solubility of starch acetate. The WSI denotes the amount of soluble carbohydrate staying in the water phase when starch is submerged in water. The low solubility of native corn starch may be explained by its semicrystalline internal structure and/or its ability to form a lipid complex ( Singh et al., 2004 ). The X-ray diffraction patterns of starch acetate showed a destruction of the ordered structure of the starch granules, characterised by a substantial reduction of the degree of crystallinity ( Table 1 ). The introduction of bulky acetyl groups into the starch molecule prevented the inter-chain association in the starch acetate, and enhanced the access of water to the amorphous area and this phenomenon would increase the hydration and the swelling behaviour of the starch granule ( Xu et al., 2005 ). On the other hand, with an increase in the degree of acetylation, the amount of hydrophilic hydroxyl groups and the movement of water molecules within the starch molecules were reduced. Consequently, the WSI and WAI of starch acetates decreased, making them more hydrophobic. Shogren and Biswas (2006) reported that the water solubility of acetylated starch began to decrease at DS over one. This phenomenon was attributed to the increasing hydrophobicity from the incorporated acetyl groups. Swelling in water is mainly due to amylopectin ( Sjöqvist & Gatenholm, 2005 ) and it was described above that amylose is preferentially the priority site of acetylation. Thus, for not highly substituted starches, the amylopectin content is still substantial and this could raise the water uptake in the granule if more water is accessible. The surface porosity of starch acetates could also promote the penetration of the water molecules. But this faculty could be reduced by the aggregation observed in high DS starch acetates. Therefore, the fluctuations of the WSI and WAI values of corn starch acetates were dependent on the conjunction of the above mentioned effects. 4 Conclusion The influences of different molar ratios of acetic acid and acetic anhydride on the acetylation of corn starch were investigated in this paper. Starch acetates with high DS were synthesised under microwave radiation, using iodine as a catalyst. We observed that the DS presented a critical point for all molar ratios of acetic acid and acetic anhydride; therefore, the DS of starches could be controlled by varying the ratios of acetic acid and acetic anhydride (mole/mole). The ratio 1:1 seemed to be the best ratio. Both crystallinity and surface morphology of starch were affected by the ratio of these two reagents. The products obtained from our reaction showed good thermoplastic and thermostable properties, and they are suitable for processing in non-food applications. In an environmentally friendly context, the control in the use of reagents must conform to the principles of green chemistry. References Aburto et al., 1999 J. Aburto H. Hamaili G.M. Baziard F. Senocq I. Alric E. Borredon Free-solvent synthesis and properties of higher fatty esters of starch Starch/Stärke 51 8–9 1999 302 307 Part 2 Biswas et al., 2007 A. Biswas G. Selling M. Appell K.K. Woods J.L. Willett C.M. Buchanan Iodine catalysed esterification of cellulose using reduced levels of solvent Carbohydrate Polymers 68 2007 555 560 Biswas et al., 2008 A. Biswas R.L. Shongren G. Selling J. Salch J.L. Willett C.M. Buchanan Rapid and environmentally friendly preparation of starch esters Carbohydrate Polymers 74 2008 137 141 Brelid and Simonson, 1999 P.L. Brelid R. Simonson Acetylation of solid wood using microwave heating Holz als Roh-und Werkstoff 57 1999 383 389 Cauvain, 2003 Cauvain, S. P. (2003). Bread making improving quality (pp. 291–300). Wood Head Publishing Limited. ISBN-13: 978 1 85573 8. Cheetham and Tao, 1998 N.W.H. Cheetham L. Tao Variation in crystalline type with amylose content in maize starch granules: An X-ray powder diffraction study Carbohydrate Polymers 36 1998 277 284 Chen et al., 2004 Z.H. Chen H.A. Schols A.G.J. Voragen Differently sized granules from acetylated potato and sweet potato starches differ in the acetyl substitution pattern of their amylose populations Carbohydrate Polymers 56 2004 219 226 Chi et al., 2008 H. Chi K. Xu X. Wu Q. Chen D. Xue C. Song Effect of acetylation on the properties of corn starch Food Chemistry 106 2008 923 928 Chi et al., 2007 H. Chi K. Xu D. Xue C. Song W. Zhang P. Wang Synthesis of dodecenyl succinic anhydride (DDSA) corn starch Food Research International 40 2007 232 238 Chung et al., 2003 H.J. Chung K.S. WooSoo S.T. Lim Glass transition and enthalpy relaxation of cross-linked corn starches Carbohydrate Polymers 55 2003 9 15 Chung et al., 2006 Y.L. Chung H.M. Lai Molecular and granular characteristics of corn starch modified by HCl–methanol at different temperatures Carbohydrate Polymers 63 2006 527 534 Elomaa et al., 2004 M. Elomaa T. Asplund P. Soininen R. Laatikainen S. Peltonen S. Hyvärinen Determination of the degree of substitution of acetylated starch by hydrolysis, 1 H-NMR and TGA/IR Carbohydrate Polymers 57 2004 261 267 Feuer and Heights, 1998 Feuer, B. I., & Heights, B. (1998). Method of making starch acetate using an acid catalyst. US Patent office, Pat. No.5 710 269. Forssell et al., 1997 P.M. Forssell J.M. Mikkilä G.K. Moates R. Parker Phase transition behaviour of concentrated barley starch–glycerol–water mixtures, a model for thermoplastic starch Carbohydrate Polymers 34 1997 275 282 Jie et al., 2006 M.G. Jie W. Peng M.X. Sheng Z. Xing Z. Tong Crosslinking of corn starch with sodium trimetaphosphate in solid state by microwave irradiation Journal of Applied Polymer Science 102 2006 5854 5860 Li et al., 2009 J. Li L.P. Zhang F. Peng J. Bian T.Q. Yuan F. Xu Microwave-assisted solvent-free acetylation of cellulose with acetic anhydride in the presence of iodine as a catalyst Molecules 14 2009 3551 3566 Nutan, 2004 Nutan, M. T. H. (2004). Starch acetate as a film forming excipient in controlled drug delivery. PhD Dissertation Thesis. Qiang et al., 1999 L.Z. Qiang Y.X. Su F. YI Effect of bound water on thermal behaviors of native starch, amylose and amylopectin Starch/Stärke 51 11–12 1999 406 410 Saartrat et al., 2005 S. Saartrat C. Puttanlek V. Rungsardthong D. Uttapap Paste and gel properties of low-substituted acetylated canna starches Carbohydrate Polymers 61 2005 211 221 Schuck et al., 2007 P. Schuck S. Mejean A. Dolivet R. Jeantet B. Bhandari Keeping quality of dairy ingredients Lait 87 2007 481 488 Shogren and Biswas, 2006 R.L. Shogren A. Biswas Preparation of water soluble and water-swellable starch acetates using microwave heating Carbohydrate Polymers 64 2006 16 21 Shogren, 2008 R. Shogren Scandium triflate catalyzed acetylation of starch at low to moderate temperatures Carbohydrate Polymers 72 2008 439 443 Singh et al., 2007 J. Singh L. Kaur O.J. McCarthy Factors influencing the physico-chemical, morphological, thermal and rheological properties of some chemically modified starches for food applications-a review Food Hydrocolloids 21 2007 1 22 Singh et al., 2004 N. Singh D. Chawla J. Singh Influence of acetic anhydride on physicochemical, morphological and thermal properties of corn and potato starch Food Chemistry 86 2004 601 608 Sjöqvist and Gatenholm, 2005 Sjöqvist, M., & Gatenholm, P. (2005).The effect of starch composition on structure of foams prepared by microwave treatment. Journal of Polymers and the Environment, 13 (1). doi:10.1007/s10924-004-1213-8. Wang et al., 2008 X. Wang W.Y. Gao L.M. Zhang P.G. Xiao L.P. Yao Y. Liu Study on the morphology, crystalline structure and thermal properties of yam starch acetates with different degrees of substitution Science in China Series B-Chemistry 51 9 2008 859 865 Xu et al., 2005 Y.X. Xu Y. Dzenis M.A. Hanna Water solubility, thermal characteristics and biodegradability of extruded starch acetate foams Industrial Crops and Products 21 2005 361 368 Xu et al., 2004 Y. Xu V. Miladinov M. Hanna Synthesis and characterization of starch acetates with high substitution Cereal Chemistry 81 6 2004 735 740 Yan and Zhengbiao, 2010 H. Yan G.U. Zhengbiao Morphology of modified starches prepared by different methods Food Research International 43 20 2010 767 772 Zhang et al., 2009 L.M. Zhang W.G. Xie X. Zhao Y. Liu W. Gao Study on the morphology, crystalline structure and thermal properties of yellow ginger starch acetates with different degrees of substitution Thermochimica Acta 495 2009 57 62