Preparation of A Biporous Polymeric Adsorbent by Double Emulsification for Flowthrough Chromatography of Proteins

GY Sun,QS Shi,Y Sun

DOI: https://doi.org/10.3724/sp.j.1105.2006.00279

2006-01-01

Abstract:This paper reports a technique to fabricate the stationary phase for high-speed protein flowthrough chromatography. Using glycerol aqueous solution (20 wt%) and n-heptane/toluene organic solvent as the porogenic agents, a novel type of biporous, matrix (BiPB) has been prepared by ultraviolet photo-polymerizing monomers (glycidyl methacrylate and ethylene glycol dimethacrylate) by a (W/O)/W emulsification technique. It was found that there were two types of pores ( micropores and superpores) in BiPB, but there was only micropores in the microporous beads (MiPB) created by O/W emulsification. The pores of BiPB were in the range of 10 similar to 100 nm and 1000 similar to 7300 nm, whereas those of MiPB were mainly 10 similar to 100 nm in size. The specific surface area, hydrated density and particle size of BiPB were 41.9 m(2)/g, 1.08 g/mL and 42.8 mu m, respectively, similar to those of MiPB (52.1 m(2)/g, 1.11 g/mL and 42.4 mu m) The static adsorption capacity of BiPB for bovine serum albumin (BSA) was also similar to that of MiPB. At a low flow rate (5 cm/min), the dynamic adsorption capacity (DAC) of BiPB for BSA was close to that of MiPB. At high flow rate (40 cm/min), however, the DAC of BiPB was about three times as high as that of MiPB. The results indicate that BiPB columns were promising for high-speed protein chromatography.