Photocathodic Protection on Stainless Steel by Heterostructured NiO/TiO<sub>2</sub> Nanotube Array Film with Charge Storage Capability
Piao Jin,Zichao Guan,Yan Liang,Kai Tan,Xia Wang,Guangling Song,Ronggui Du
DOI: https://doi.org/10.3866/PKU.WHXB201906033
2021-01-01
Acta Physico-Chimica Sinica
Abstract:Photocathodic protection by TiO2 semiconductor materials for metals has interested many corrosion researchers for years. However, a pure TiO2 semiconductor anode can only absorb ultraviolet light and cannot maintain the photocathodic protection in the dark. This has limited its practical applications to a great extent. Overcoming these limitations is significant as well as challenging. Therefore, the objective of this work is to prepare a modified TiO2 composite film with visible light absorption and charge storage capabilities for application in photocathodic protection. First, we fabricated an ordered TiO2 nanotube array film on a Ti substrate by electrochemical anodization. Then, we prepared NiO nanoparticles on the film via a hydrothermal reaction to obtain a p-n heterostructured NiO/TiO2 nanotube array composite film. The properties of the prepared films were investigated by scanning electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, UV-Vis absorption spectroscopy, photoluminescence spectroscopy, and photoelectrochemical techniques. The results indicated that the electrochemically anodized TiO2 film had an anatase phase structure and consisted of vertically ordered nanotubes with an inner diameter of about 80 nm and length of 250 nm. After the NiO nanoparticles were deposited on the film, the TiO2 nanotube array structure remained intact. The main phase of TiO2 was still anatase, but the light absorption of the NiO/TiO2 composite film was extended into the visible region, which was in contrast to that of the simple TiO2 film. Moreover, the composite film showed lower photoluminescence intensities than the TiO2 film, implying that a higher charge carrier separation efficiency could be achieved by modification with NiO. Under white light illumination, the photocurrent density of the NiO/TiO2 composite film in a mixed solution of 0.5 mol.L-1 KOH and 1 mol.L-1 CH3OH reached 176 mu A.cm(-2), which was 2 times higher than that of the simple TiO2 nanotube film, indicating that the composite film had improved photoelectric conversion efficiency and photoelectrochemical properties. The potential of 403 stainless steel (403SS) in 0.5 mol.L-1 NaCl solution decreased by 380 and 440 mV relative to its corrosion potential when coupled to the TiO2 film and NiO/TiO2 composite film, respectively, under white light illumination. This indicated that the heterostructured NiO/TiO2 film as a photoanode could produce more effective photocathodic protection on the steel as compared with the pure TiO2 film. Even after 2.5 h of illumination, the composite film could continuously provide photocathodic protection to 403SS for about 15.5 h in the dark, suggesting that the NiO/TiO2 composite film had a charge storage capability that was significant for its practical applications.