Impact of erbium oxide on structure, linear and nonlinear optical properties of bismo-borate glass systems for using in optical applications
Hanan Al-Ghamdi,Norah A. M. Alsaif,Adel M. El-Refaey,R. A. Elsad,M. S. Shams,Y. S. Rammah,Shaaban M. Shaaban,A. S. Abouhaswa,M. S. Sadeq
DOI: https://doi.org/10.1007/s11082-024-06335-5
IF: 3
2024-02-14
Optical and Quantum Electronics
Abstract:In the present article, samples of erbium (Er)-doped bismo-borate glasses have been fabricated with general chemical compositions: 70B 2 O 3 –10CaO–10Li 2 O−(10-x)Bi 2 O 3 − xEr 2 O 3 : 0 (Er-0.0) ≤ x ≤ 1 (Er-1.0) mol% using the conventional melt-quench process. The impact of Er 3+ ions on the structure and optical (linear and nonlinear) characteristics of Er-0.0/Er-1.0 glass blocks have been investigated. XRD measurements showed the lack in crystallinity of the prepared samples. In the range of UV-Vis measurements, there are absorption bands attributed to the electronic transitions (4f−4f) of Er 3+ ions. The absorption bands seen at wavelengths of approximately 366, 379, 409, 452, 490, 523, 545, 653, 797, and 978 nm are associated with electronic transitions from the ground state, 4 I 15/2 , to several excited states, namely 4 G 9/2 , 2 G 11/2 , 2 H 9/2 , 4 F 5/2 , 4 F 7/2 , 2 H 11/2 , 4 S 3/2 , 4 F 9/2 , 4 I 9/2 , and 4 I 11/2 , respectively. The optical band gap (E g ) values ranged from 2.61 to 3.11 eV for Er0.0 to Er1.0 glass samples, respectively. Values of linear refractive index (n 0 ) ranged from 2.498 to 2.374. Values of the nonlinear refractive index varied from 7.76 to 4.99, while the third order non-linear optical susceptibility (χ (3) ) values ranged from 5.14 to 3.14 for Er0.0 to Er1.0 glasses, respectively. Therefore, the suggested glasses can be used in several optical applications such as opto-electronic devices.
engineering, electrical & electronic,optics,quantum science & technology