Abstract:Aim: To observe the biocompatibility of β-tricalcium phosphate (TCP)/calcium polyphosphate fiber (CPPF)/poly-levolactic acid (PLLA) composite as a novel bone tissue engineered scaffold by observing the morphology and proliferation of in vitro cultured cells. Methods: The experiment was carried out in the experimental center of Medical College and Institute of Endemic Diseases, Xi'an Jiaotong University from January 2002 to January 2004. 1 β-TCP/CPPF/PLLA scaffold was prepared by the Institute of Composite Materials, Lanzhou Jiaotong University; CPPF was (15.0±1.2) μm in diameter with (3.0± 0.46)% mean biodegradation rate, (1.0±0.2) GPa tensile strength, and (48.0±7.6) GPa; the mean molecular mass of PLLA was 27.6×104. The weight ratio of scaffold composite was β-TCP:CPPF:PLLA=2:3:5. 2 With the proportion of 1 g composite:10 mL extraction mediator, β-TCP/CPPF/PLLA scaffold was extracted by using DMEM containing 0.1 volume fracture fetal bovine serum at 37°C for 24 to 72 hours to prepare the extraction fluid, which was filtered before using. The bone marrow stromal cells (BMSCs) were divided into 3 groups and cultured with β-TCP/CPPF/PLLA maceration extract (experiment group), DMEM culture medium (negative control group) and 6.4 g/L Phenol solutions (positive control group), and the dilution of the maceration extract was divided into 100%, 75%, 50%, and 25%, respectively. 3 The growth and change condition of BMSCs were observed by phase contrast microscope. The growth and proliferation of BMSCs were investigated with MTT method to determine A value and calculate the proliferation rate of cells. Results: 1 On days 1, 2 and 3, the cell number of the positive control group displayed noticeable decrease, and the cells were of pyknosis even disaggregation; the cell number of the experiment group and negative control group was remarkably increased with normal call appearance. 2 At each time point of culture, the cytotoxicity of all groups were grade 0 with more than 80% cell proliferation rate except the positive control group was grade 4 with 0-20% cell proliferation rate; except the positive control group, the A values of experiment groups and negative control group were increased with culture days, and the A value of the positive control group on days 1, 2 and 3 was much lower than other groups (P < 0.01);. there were no significant differences between negative control group and experiment group (P > 0.05). Conclusion: β-TCP/CPPF/PLLA scaffold composite has a negligible influence and differentiation of BMSCs. It has good cell compatibility and no cytotoxicity.

An Experimental Study on Osteoblast Proliferation Activity of Coral Hydroxyapatite and Pure-Phase Beta-Tricalcium Phosphate

Effect of coral hydroxyapatite on the osteogenic property of platelet-rich plasma-induced human bone marrow stromal stem cells

Biocompatibility of Adult Human Osteoblasts with Coral-Derived Hydroxyapatite in Vitro

Cytocompatibility of stem cells-derived osteoblasts with porous calcium carbonate ceramics

The Study of Osteogenous Active on the Surface of Carbonated Hydroxyapatite

A New Tissue Engineering Scaffold-Biodegradable Coral-Hydroxyapatite

Biological compatibility and micromorphologic observation of three dimensional porous beta-tricalcium phosphate scaffolds and mesenchymal stem cells in constructing tissue engineered bone

Experimental study of biocompatibility on natural coral and allogeneic demineralized bone matrix as scaffold of bone marrow stroma cell in bone tissue engineering

A quantitative study on the biological degradation of a series of controllable absorbability coral-hydroxyapatite

Compatibility of Osteoblast with the Compound of Bone Tissue-Engineering Material and Growth Factor

Experimental Study on the Osteoinduction of Calcium Phosphate Biomaterials in Vivo and the Capability of Supporting Osteoblast Proliferation in Vitro

Comparative in Vitro Osteoinductivity Study of CaP Ceramics (HA, Α-Tcp, Β-Tcp) Using 10T1/2 Cells with Different Controls and Possible Correlations with Other Systems

Biocompatibility Evaluation in Vitro. Part I: Morphology Expression and Proliferation of Human and Rat Osteoblasts on the Biomaterials

Surface Modified β-Tricalcium Phosphate Ceramic on Proliferation and Differentiation of Bone Marrow Stromal Cells

[Preliminary study of osteoblastic effect in different contents of calcium silicate bioceramics].

Cell biocompatibility of beta-tricalcium phosphate/calcium polyphosphate fiber/polylevolactic acid composite as a novel bone tissue-engineered scaffold

The experimental study of the preparation and cellular biological compatibility of calcium phosphate cement(CPC)

An innovative biomimetic porous bioceramic to facilitate bone tissue regeneration: Microstructural characteristics, biocompatibility, and in vivo rabbit model evaluation

Effect of β-tricalcium phosphate ceramic on the biological behavior of periosteal cells from Beagle dogs

Comparative study of three kinds of scaffold materi als for bone tissue engineering

Study on the Effects of Strontium Substituted by Droxyapatite of Different Porities on the Biological Behavior of Osteoblasts in Vitro