Abstract:Novel phosphorus-containing liquid crystalline copolyesters based on biphenyl mesogenic monomer (PDEBP) were synthesized by polycondensation of dimethyl biphenyl-4,4'-dicarboxylate (DBD), diethylene glycol (DEG) and a phosphorus-containing diol, 2-(6-oxido-6H-dibenz < c, e > < 1, 2 > oxaphosphorin-6-yl)-1,4-phenylenebis(oxy) diethanol (DOPO-HQ-HE). Chemical structure of the PDEBP was characterized by H-1-NMR spectroscopy, and the thermal and liquid crystalline behaviors of the copolyesters were investigated by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and hot-stage polarizing optical microscope (POM) TGA results suggested that char formation of the copolyesters was improved with the introduction of DOPO-HQ-HE without destroying the initial thermal stability of the polymer, and the residue at 700 degrees C in N-2(W-tR(700)) of PDEBP7.5 (7.5 mol% of DOPO-HQ-HE in copolyester) reached 31. 9 wt%, having a positive influence on flame retardance of the copolyesters. DSC tests suggested that the crystallinity of the copolyesters was destroyed by incorporating DOPO-HQ-HE into the main chain due to the bulky pendent group. The isotropic temperature (T-i) and endothermic heat (Delta H-i) were decreased by increasing the amount of DOPO-HQ-HE, and the T-i, and Delta H-i, of PDEBP7. 5 reached 129 degrees C and 1. 61 J/g, respectively. POM observations showed that a typical birefringence phenomenon of nematic schlieren structure could be found in the processes of both heating and cooling, in accord with the results of DSC tests except these of PDEBP7. 5, for which it was hard to find the birefringence phenomenon during heating and cooling by POM, indicating the further introduction of the phosphorus-containing diol could destroy the liquid crystalline behavior of the resulting copolyester.

A Kinked Unit-Containing Thermotropic Liquid Crystalline Copolyester With Low Glass Transition Temperature And Broad Phase Transition Temperature

Temperature-Dependent Triple Crystal Polymorphism of Poly(hexamethylene Terephthalate): Long-Range Ordered Mesophase Formation and Crystal Structure–Property Relationships

Colorless Transparent Cyclobutanediol-Based Copolyesters with Excellent Polymerization Robustness, Thermal Stability, and High Performance

Synthesis and Characterization of Phosphorus-Containing Liquid Crystalline Copolyesters Based on Biphenyl-4, 4 '-Dicarboxylic Acid

Synthesis and Thermal Behavior of Phosphorus-Containing Thermotropic Wholly Aromatic Copolyesters

Novel Inherently Flame-Retardant Poly(trimethylene Terephthalate) Copolyester with the Phosphorus-Containing Linking Pendent Group

Main-Chain Liquid Crystalline Copolyesters With A Phosphorus-Containing Non-Coplanar Moiety

A Novel Phosphorus‐containing Thermotropic Liquid Crystalline Poly(ester‐imide) with High Flame Retardancy

A novel phosphorus-containing poly(1,4-cyclohexylenedimethylene terephthalate) copolyester: Synthesis, thermal stability, flammability and pyrolysis behavior

Synthesis and properties of wholly aromatic phosphorus-containing thermotropic liquid crystal copolyesters with excellent fibre formation ability

SYNTHESIS OF PHOSPHORUS-CONTAINING THERMOTROPIC LIQUID CRYSTALLINE COPOLYESTERS Via SOLID-STATE POLYMERIZATION

Morphological Evolution of Thermotropic Liquid Crystalline Copolyester and Its Effects on Rheological, Thermal and Flame-Retarding Behaviors of Polycarbonate

Synthesis Of Novel Ph-Tunable Thermoresponsive Hydroxyl-Terminated Hyperbranched Polyether

Synthesis and characterization of thermotropic liquid crystalline copolyester containing bis(4-hydroxyphenyl) methanone series (I)

In Situ Reinforced and Flame-Retarded Polycarbonate by a Novel Phosphorus-Containing Thermotropic Liquid Crystalline Copolyester

Erratum: A Novel Thermotropic Liquid Crystalline Copolyester Containing Phosphorus and Aromatic Ether Moity Toward High Flame Retardancy and Low Mesophase Temperature

Synthesis and Characterization of Main-Chain Liquid Crystalline Copolyesters Containing Phosphaphenanthrene Side-Groups

A Novel Aromatic–aliphatic Copolyester Consisting of Poly(1,4‐dioxan‐2‐one) and Poly(ethylene‐co‐1,6‐hexene Terephthalate): Preparation, Thermal, and Mechanical Properties

In-depth analysis on thermal phase transition mechanism of main-chain phosphorus-containing thermotropic liquid crystal copolyester

Phosphorus-containing Poly(trimethylene Terephthalate) Derived from 2-(6-oxido-6h-dibenz〈c,e〉〈1,2〉oxaphosphorin-6-yl)-1,4-hydroxyethoxy Phenylene: Synthesis, Thermal Degradation, Combustion and Pyrolysis Behavior

SYNTHESIS AND CHARACTERIZATION OF A FLAME-RETARDANT AND ANTI-DRIPPING COPOLYESTER