Abstract:Increasing the porosity of porous ceramics is desirable for application as permeable materials. In this paper, we demonstrate a technique that utilizes the reactions between Si3N4 and carbon to result in a restrained shrinkage and finally high porosity. Porous Si3N4 ceramics was obtained by a small amount of carbon addition (1-5vol%) and 5wt% Y2O3, Increasing the carbon content, porous Si3N4/SiC nanocomposites were obtained. High porous SiC ceramics were fabricated employing pressureless sintering of powder compacts of alpha Si3N4 and carbon powder (Si3N4:C=1:3 by mol), with Y2O3 and Al2O3 as the sintering aids. The shrinking can be greatly restrained by the reaction bonding, this method can be referred to be restrained sintering by reaction bonding (RSRB). Densification, porosity, pore size, mechanical properties was investigated.

Highly Porous Silicon-Based Ceramics Fabricated with Restrained Sintering by Reaction Bonding (Rsrb)