Synthesis of a Fully Capped Mesoporous Silica and Its Hybrids with Extremely Low Dielectric Constant and Loss
Wei Shan,Lei Chen,Yang Chu,Feipeng Zhao,Guozheng Liang,Aijuan Gu,Li Yuan
DOI: https://doi.org/10.1016/j.micromeso.2013.04.014
IF: 5.876
2013-01-01
Microporous and Mesoporous Materials
Abstract:A novel fully capped mesoporous silica (FCMPS) was synthesized by producing a layer of linked polyhedral oligomeric silsesquioxanes (LPOSS) on the surface of a typical mesoporous silica (SBA-15). The structure of FCMPS was characterized using Fourier Transform Infrared (FTIR), Nuclear Magnetic Resonance (29Si NMR), X-ray Diffraction (XRD), Scanning Electron Microscope (SEM), High Resolution Transmission Electron Microscope (HRTEM), Nitrogen adsorption–desorption and thermogravimetric (TG) analyses. Compared with SBA-15, FCMPS has not only high surface area, pore volume and size, but also remarkably improved thermal stability, the initial degradation temperature (Tdi) of FCMPS increases about 194°C. In addition, FCMPS overcomes the drawback of SBA-15, exhibiting much lower and stable dielectric constant and loss. Based on the synthesis of FCMPS, the FCMPS/bismaleimide resin (BD) hybrids with different contents of FCMPS were prepared, and their dielectric properties were investigated. Results show that FCMPS/BD hybrids have much lower and stable dielectric constant and loss than SBA-15/BD hybrids owing to the special structure of FCMPS. With the addition of 1wt.% FCMPS into BD resin, the dielectric constant of the resultant hybrid is as low as about 2.50 over the whole frequency from 10 to 106Hz; moreover, the dielectric loss of the hybrid is almost independent on the frequency, and the dielectric loss at higher frequencies (>103Hz) is even lower than that of BD resin. These attractive features make FCMPS have obvious advantage in developing materials with low dielectric constant and loss.