Preparation and Investigation of Conductive Hydrogels of Polyacrylamide-g-Polyaniline
Xiao-xia Lu,Peng-yun Li,Jia-min Li,Wei-dong He
DOI: https://doi.org/10.11777/j.issn1000-3304.2016.16086
2016-01-01
Abstract:Composite hydrogels of polyacrylamide-graft-polyaniline possessing both good mechanical strength and excellent electrical conductivity were prepared through a two-step polymerization route. Firstly, acrylamide (Am) and N-(4-aminophenyl) acrylamide (APAm) were radically copolymerized through Co-60 gamma-irradiated initiation in aqueous solution to form P (Am-co-APAm) hydrogels, of which the aminophenyl side groups facilitated the following graft polymerization of aniline. Secondly, after the lyophilized P (Am-co-APAm) hydrogels were re-swelled in aniline aqueous solution, aniline absorbed in the macroporous hydrogels underwent the oxidation coupling graft polymerization with aminophenyl side groups of P (Am-co-APAm) to result in P(Am-co-APAm)-g-PANI composite hydrogels. As expected, the produced polyaniline was naturally deposited onto the pore wall of P (Am-co-APAm) hydrogels, leading to the formation of inter-connected conductive pathway. Fourier transfer infrared spectroscopy, combined with the repeated removal of possible homopolyaniline with N-methylpyrilidone, confirmed the successful grafting. To modulating the mechanical properties, the influences of radical polymerization parameters were investigated. By changing radiation duration and dose rate, it was found that the gel fraction (GF) of P (Am-co-APAm) hydrogels increased with the increment of irradiation dose, while swelling degree (SD) had the maximum value under medium irradiation dose,reflecting that both monomer conversion and crosslinking degree affected the GF and SD of P (Am-coAPAm) hydrogels. With the increase in monomer concentration, GF was kept going up and levelled off at 1. 5 c(o) while SD kept going down and levelled off at the same monomer concentration. The tensile strength and elongation at break of P (Am-co-APAm) hydrogels decreased, but elastic modulus increased, reflecting the cooperative impact of crosslinking degree and polymer produced. Interestingly, as observed by scanning electron microscopy,the hydrogels prepared in neutral water had the open and macro-porous morphology while those obtained in HC1 solution had no distinct pores. For both hydrogels, TEM images showed no separated polyaniline particles located in the hydrogel pores and the thickness of pore wall obviously increased, indicating the formation of continuous polyaniline layer on the previous pore wall. Therefore, after being doped with HC1, P(Am-co-APAm)-g-PANI composite hydrogels exhibited excellent conductivity as high as 7 similar to 10 S/cm, which exceeded most of the reported values for polyaniline-containing hydrogels.