A Kinetic Study on the Leaching of Scheelite Sulfuric Acid Decomposition Residue with Hydrogen Peroxide
Yuqing Qiu,Zhenqiang Wang,Changsheng Yin,Xingyu Chen,Xuheng Liu,Ailiang Chen,Jiangtao Li,Lihua He,Fenglong Sun,Zhongwei Zhao
DOI: https://doi.org/10.1007/s40831-023-00744-8
2023-01-01
Abstract:The sulfuric acid decomposition method of scheelite can solve the problems existing in the traditional alkali (NaOH) method of tungsten smelting. However, selectively leaching tungsten from the decomposition residue is difficult. In this study, a hydrogen peroxide selective leaching technique was proposed for the extraction of tungsten from scheelite sulfuric acid decomposition residue. The effects of stirring speed, mineral particle size, temperature, and H2O2 concentration on this reaction were studied, meanwhile the leaching kinetics of this process were investigated emphatically. It was confirmed that the stirring speed had little influence on the leaching of H2O2 on sulfuric acid decomposition residue, while an increase in temperature and H2O2 concentration significantly enhanced the tungsten leaching ratio within this system. The leaching process can be described using Avrami equation, and the reaction characteristic parameter was obtained to be 0.71 via fitting the equation. Meanwhile, by fitting the experimental data to the Arrhenius equation, it could be derived that the influence index of mineral particle size was − 0.95, the reaction order of H2O2 concentration was 0.46, and the influence constant of stirring speed was − 0.13. The apparent activation energy of the reaction was 24.62 kJ/mol, revealing that the mixed-controlled reaction aptly described the leaching process.