Poly (hydroxybutyrate-hydroxyvalerate) membrane for guiding bone regeneration in vivo
Qian Tang,Jian-hong Chen,Huan-you Liang,Jian Wu,Yuan Li,Xiao-feng Chen,Gang Wu
DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.23.005
2008-01-01
Abstract:BACKGROUND: The shape and amount of bone regenerated depend on the existence and maintenance of hypolemmal space. Collapse and reduction of hypolemmal space will greatly inhibit bone regeneration. Therefore, the key to success of induced bone regeneration is to select membrane material.OBJECTIVE: This study is designed to investigate the feasibility of poly (hydroxybutyrate-hydroxyvalerate) (PHBV) membrane for guiding bone regeneration.DESIGN, TIME AND SETTING: This study, a self-control animal experiment, was performed at the Laboratory Animal Center, Third Hospital Affiliated to Sun Yat-sen University between May 2005 and October 2006.MATERIALS: PHBV membrane, (10×10×0.3)mm, was provided by Research of Biomaterials, College of Material Science and Engineering, South China University of Technology. Eight healthy hybrid dogs, aged 1 year old, weighing 10-12kg, were included for model of tibial defects.METHODS: Four bone defects were made on bilateral tibias in each dog. Bilateral proximal bone defects of all dogs were included as control group and only subjected to periosteal flap reduction. Bilateral distal bone defects of all dogs were included as experimental group and covered by PHBV membrane. Samples were harvested at weeks 2, 4, 8, and 12 post-surgery.MAIN OUTCOME MEASURES: In vivo degradation performance and ossific capability of PHBV copolymer as well as energy-dispersive X-ray analysis and elemental quantitative assay in bone defect regions.RESULTS: In the experimental group, at week 8 post-surgery, PHBV copolymer membrane had been gradually degraded, different sizes of hollows formed on its surface, bone defect surface was smooth and flat, and X-ray results showed increased bone density in the bone defect regions; at week 12 post-surgery, the PHBV copolymer was still not degraded completely, but bone defect regions had been completely fused with normal bone. Energy-dispersive X-ray analysis and elemental quantitative assay results demonstrated in the experimental group, peaks of Ca and P atom number of newly formed bone were predominant, and peaks of impurity were few. With time going, element Ca and P levels in the newly formed bone were increased, the ratio for Ca and P atoms approximated to that in the normal bone. There was significant difference between the. experimental group and the control group (P<0.05).CONCLUSION: PHBV copolymer membrane is a promising ideal natural membrane material for guiding bone regeneration.