A composite proton exchange membrane with three-dimensionally-reinforced hydrogen bonding network for durable hydrogen fuel cells
Yunfa Dong,Chao Feng,Haodong Xie,Yuhui He,Carlos M. Costa,Senentxu Lanceros-Mendez,Jiecai Han,Weidong He
DOI: https://doi.org/10.1039/d4qi01074d
IF: 7.779
2024-06-10
Inorganic Chemistry Frontiers
Abstract:Expanded polytetrafluoroethylene (e-PTFE) reinforced perfluorosulfonic acid (PFSA) is the predominant proton exchange membrane (PEM) of hydrogen fuel cells. However, the difference in interfacial properties between PFSA and e-PTFE significantly decrease the proton conduction efficiency, and durability of PEM. In this study, the polyphenolamine treatment method (TA) is employed to effectively enhance the hydrophilicity and interfacial compatibility of e-PTFE, as well as to functionalize the surface of the free radical scavenger ZrO2 filler. The surface of the modified e-PTFE and ZrO2 is rich in polar phenolic hydroxyl groups and amino groups, which effectively enhance the three-dimensional interface compatibility of the e-PTFE/PFSA reinforced composite membrane (RCM), and improve the proton conductivity by establishing an additional hydrogen bonding network. The proton conductivity of the RCM is 0.203 S cm-1 at 80 °C, and the tensile strength is 50.7 MPa. The peak power density of the hydrogen fuel cell based on the composite membrane is 1.46 W cm-2 at 80 °C and 50% RH. Moreover, the durability of the composite membrane is considerably improved by the redox properties of the surface functional groups of e-PTFE and the valence-changing properties of ZrO2. Following a 72-hour Fenton reaction, the mass loss of TA@ZrO2/e-PTFE RCM was found to be only 13.5 %. The accelerated durability test indicates that TA@ZrO2/e-PTFE RCM can still provide a current density of 1.3 A cm-2 after 5500 dry/wet cycles at 0.55 V.
chemistry, inorganic & nuclear