Abstract:An organic-inorganic hydrophobic mesoporous silica has been successfully prepared by a co-condensation method with tetraethoxysilane (TEOS) and vinyltriethoxysilane (VTES) as mixed precursors under acidic condition. The synthesized mesoporous silica has been characterized by small-angle X-ray diffraction, transmission electron microscopy, N-2 sorption isotherms, magic-angle spinning nuclear magnetic resonance, and X-ray photoelectron spectroscopy. It is found that the newly synthesized adsorbents exhibit a uniform mesostructure with the vinyl groups embedded into the network of mesoporous silica. Results also show that mesoporous silica could convert from a 2D hexagonal structure (p6m) to a three-dimensional cubic structure (Ia3d) with the increase of the VTES/(VTES+TEOS) molar ratio. This structure transition could significantly increase the surface area, which also proves that VTES exerts a structure-directing effect on co-condensation synthesis. This functionalized mesoporous silica (v-SiO2) has been applied its ability in adsorbing p-xylene. It is observed that these silica materials show improved humidity resistance with the Q(wet)/Q(d)(ry) increasing from 56.2 to 85.2% (Q(d)(ry) and Q(wet) stand for the adsorption capacity under dry and wet conditions, respectively). After the adsorption, the adsorbed p-xylene was desorbed from the adsorbents by a vacuum pump. Results show that the desorption ratio of p-xylene could reach up to 88.1% under wet conditions for the adsorbent with the molar ratio VTES/(VTES+TEOS) of 15% (v-SiO2 (15%)). The adsorption/desorption recycling tests prove that the v-SiO2 could possess prominent stability with over 96% adsorption capacity being kept after several cycles.

Study on Adsorption of Water Vapor of Mesoporous SiO2 Prepared by Sol-Gel Method

Synthesis and Water Vapor Adsorption Property of Meso-Porous Adsorbent SiO2-TiO2

Experimental and Numerical Study on Water Sorption over Modified Mesoporous Silica

Preparation of Hydrophobic Hierarchical Pore Carbon–silica Composite and Its Adsorption Performance Toward Volatile Organic Compounds

Design and Synthesis of a Water-Resistant Mesoporous Silica Gel for the VOC Adsorption–Desorption Treatment

Preparation of SiO2 aerogels with sol-gel method and the study of their properties

Study on the preparation and external adsorption of monodisperse nano silicon dioxide

Synthesis and Water Vapor Adsorption Property of Hierarchically-Porous Aluminosilicates

Preparation and Characterization of Hydrophobic Mesoporous SiO_2

Synthesis and Characterization of Ultrafine SiO_2

Water Vapor Sorption on Surfactant-Templated Porous Silica Xerogels

Sorption/desorption equilibrium of methane in silica gel with pre-adsorption of water

Experimental study on the kinetics of water vapor sorption on the inner surface of silica nano-porous materials

Controlled synthesis of hexagonal mesostructure silica and macroporous ordered siliceous foams for VOCs adsorption

Methane adsorption on porous nano-silica in the presence of water: An experimental and ab initio study

Preparation of Mesoporous Sio2 Via of Triblock Copolymer

Preparation and Characterization of SiO<sub>2</sub>-WO<sub>3</sub> Composite Aerogel by Ambient Pressure Drying Process

Surface Modification and Adsorption Properties of SiO2 Nanoporous Aerogels

Ambient Pressure Synthesize Silica Porous Materials with Waterglass

Functionalized Ordered Mesoporous Silica by Vinyltriethoxysilane for the Removal of Volatile Organic Compounds through Adsorption/Desorption Process

Investigation On Water Vapor Adsorption Of Silica-Phosphonium Ionic Liquids Hybrid Material